Process of producing activated carbon for electrode of electric double layer capacitor
View Patent ↗A process for producing an activated carbon for an electrode of an electric double-layer capacitor, includes a step of subjecting a carbonized material to an alkali activating treatment, wherein the carbonized material has an average true specific gravity of 1.450 to 1.650 and a variation of the true specific gravities of 0.025 or less.
1. A process for producing an activated carbon for an electrode of an electric double-layer capacitor, comprising subjecting a carbonized material to an alkali activating treatment,
wherein the carbonized material has an average true specific gravity of 1.450 to 1.650 and a variation of the true specific gravity of 0.025 or less.
2. The method according to claim 1 , wherein the variation is a difference between a maximum value and a minimum value of the true specific gravity.
3. The method according to claim 1 , further comprising subjecting a raw carbon material to a carbonizing treatment so as to form the carbonized material,
wherein the carbonizing treatment is carried out in a furnace at a heating temperature of 600° C. to 1000° C., and the furnace has a temperature difference between an upper portion and a lower portion of the furnace of 1° C. to 50° C.
4. The method according to claim 3 , wherein the temperature difference between the upper portion and the lower portion of the furnace is about 20° C.
5. The method according to claim 4 , wherein the carbonizing treatment is carried out for 10 to 300 minutes in the furnace, and the furnace has a upper portion temperature of about 790° C., a middle portion temperature of about 780° C., and a lower portion temperature of about 770° C.
6. The method according to claim 3 , wherein the carbon material is a fiber aggregate having a thickness of 1 to 50 cm.
7. The method according to claim 6 , wherein the thickness is 3 to 20 cm.