Water-soluble sulfonic group-containing copolymers and terpolymers the production thereof and water-based painting and coating systems
View Patent ↗Water-soluble copolymers and terpolymers as stabilizers for aqueous building material systems and water-based paint and coating systems are described. Advantages of the copolymers and terpolymers used according to the invention compared to conventional products are firstly the very good stabilizing properties of the building material systems or water-based paint and coating systems produced correspondingly and secondly the fact that the viscosity of the systems is barely increased, so that these have excellent processability.
1. A composition that is an aqueous building material system, a water-based paint or coating system comprising a sufficient amount of a bipolymer or terpolymer to provide a stabilizing effect, wherein the bipolymer or terpolymer is water-soluble, contains sulfo groups and has a number average molecular weight of from 50,000 to 20,000,000 g/mol and consists of:
a) from 3 to 96 mol % of a structural group of formula I
wherein R 1 is hydrogen or methyl,
R 2 , R 3 , R 4 is hydrogen, an aliphatic hydrocarbon residue having from 1 to 6 carbon atoms, or a phenyl residue which may be unsubstituted or substituted by methyl groups,
V is NH or oxygen,
M is hydrogen, a monovalent or divalent metal cation, ammonium or an organic amine residue,
n is from 1 to 5,
A is ½ or 1,
b) from 3 to 96 mol % of a structural group of formula II
wherein W is —CO(O)—(CH 2 ) x — or —CO—NR 2 —(CH 2 ) x —,
x is from 1 to 6,
R 5 and R 6 are independently hydrogen, a substituted or unsubstituted aliphatic hydrocarbon residue having from 1 to 20 carbon atoms, a cycloaliphatic hydrocarbon residue having from 5 to 8 carbon atoms, or an aryl residue having from 6 to 14 carbon atoms, and
R 1 and R 2 are as defined above,
and/or
c) from 0.05 to 75 mol % of a structural group of formula III
wherein Y is O, NH or NR 5 ,
V is —(CH 2 ) x —,
R 7 is R 5 or R 6 , —(CH 2 ) x —SO 3 ⊖ M a ,
X is halogen, C 1 -C 4 -alkylsulfate of C 1 -C 4 -alkylsulfonate,
and R 1 , R 5 , R 6 , M, a and x are as defined above.
2. The composition as claimed in claim 1 , wherein the copolymers and terpolymers are used in an amount of from 0.01 to 5% by weight, based on the dry weight of the building material system, paint system or coating system.
3. The composition as claimed in claim 1 , wherein the aqueous building material systems comprises cement, lime, gypsum plaster, anhydrite, as hydraulic binders.
4. The composition as claimed in claim 1 , wherein the copolymers or terpolymers are in the foiiii of an aqueous solution having a solids content of from 0.2 to 3% by weight.
5. The composition as claimed in claim 1 , wherein the structural group a) of formula I is a 2-acrylamido-2-methylpropanesulfonate.
6. The composition as claimed in claim 1 , wherein the structural group a) of formula I is 2-acrylamido-2-methylpropanesulfonic acid sodium salt.
7. The composition as claimed in claim 1 , wherein the structural group b) of formula II is [2-(methyacryloyloxy)-ethyl]-diethylamine.
8. The composition as claimed in claim 1 , wherein the structural group c) of formula III is a [3-(methacryloylamino)-propyl]trimethlammonium salt.
9. The composition as claimed in claim 1 , wherein the structural group c) of formula III is [3-(methacryloylamino)-propyl]trimethylammonium chloride.
10. A composition that is an aqueous building material system, a water-based paint or coating system comprising a sufficient amount of a biopolymer or terpolymer to provide a stabilizing effect, wherein the bipolymer or terpolymer is water-soluble, contains sulfo groups and has a number average molecular weight of from 50,000 to 20,000,000 g/mol and consists of:
a) from 3 to 96 mol% of 2-acrylamido-2-methylpropanesulfonic acid sodium salt, and
b) from 0.05 to 75 mol% of [3-(methacryloylamino)-propyl]trimethylammonium chloride.