Dual-phase hard material comprising tungsten carbide, process for the production thereof and its use
View Patent ↗The invention relates to tungsten carbide powder consisting of powder particles, which have a core comprised of tungsten cast carbide and a covering comprised of tungsten monocarbide, to the production thereof by heating a tungsten cast carbide powder in the presence of a carbon source to a temperature ranging from 1300 to 2000° C., and to the use thereof for coating surfaces of parts subjected to wear and for producing drill bits.
1. A tungsten carbide powder which consists essentially of powder particles which have a core of cast tungsten carbide and a shell of tungsten monocarbide.
2. The tungsten carbide powder according to claim 1 , wherein the bound carbon content is 4 to 6 wt. %.
3. The tungsten carbide powder according to claim 1 , wherein the bound carbon content is 4.3 to 5.5 wt. %.
4. The tungsten carbide powder according to claim 3 , wherein the particle size determined by Ro-Tap sieve analysis in accordance with ASTM B 214 is up to 3000 μm.
5. The tungsten carbide powder according to claim 4 , wherein it has a hardness of >2000 HVO.1 and the thickness of the shell of tungsten monocarbide is 0.05 to 0.4 times the average particle size.
6. The tungsten carbide powder according to claim 5 , wherein the powder particles have a sharp-edged crushed morphology.
7. The tungsten carbide powder according to claim 1 , wherein the particle size determined by Ro-Tap sieve analysis in accordance with ASTM B 214 is up to 3000 μm.
8. The tungsten carbide powder according to claim 1 , wherein the thickness of the shell of tungsten monocarbide is 0.05 to 0.4 times the average particle size.
9. The tungsten carbide powder according to claim 1 , wherein it has a hardness of >2000 HVO.1.
10. The tungsten carbide powder according to claim 1 , wherein the powder particles have a sharp-edged crushed morphology.
11. A process for the production of the tungsten carbide powder as claimed in claim 1 which comprises powder particles which have a core of cast tungsten carbide and a shell of tungsten monocarbide which comprises heating a cast tungsten carbide powder in the presence of a carbon source to a temperature of 1300 to 2000° C.
12. The process according to claim 11 , wherein cast tungsten carbide powder is heated in the presence of a carbon source to a temperature of 1400 to 1700° C.
13. The process according to claim 11 , wherein the carbon source is carbon black, graphite and/or a hydrocarbon.
14. A process according to claim 11 , wherein the carbon source is added in a quantity such that the total carbon content in the reaction mixture is 4 to 6 wt. %.
15. A process to surface coat a component subject to wear which comprises coating the surface of the component with the tungsten carbide powder according to claim 1 .
16. The tungsten carbide powder as claimed in claim 1 , wherein the powder particles have a spherical morphology.