Lubricant composition for hot forming
View Patent ↗The present invention provides a lubricant composition for hot forming which makes it possible to provide lubricity at 80° C. or more without being peeled or washed by the roll cooling water, and which is easily washed under 40° C. without having water resistance. The lubricant composition for hot forming of the present invention comprises: a solid lubricant from 10 to 40% by mass; water-dispersible synthetic resin from 5 to 20% by mass; inorganic acid amine salt from 0.5 to 5% by mass; and water from 45 to 80% by mass.
1. A lubricant composition for hot forming comprising: a solid lubricant from 10 to 40% by mass; a water-dispersible synthetic resin from 5 to 20% by mass; an inorganic acid amine salt from 0.5 to 5% by mass; and water from 45 to 80% by mass, for 100% by mass of the total mass of the lubricant composition,
wherein said water-dispersible synthetic resin is a vinyl acetate polymer obtained by emulsion polymerization using protective colloid selected from a group consisting of hydroxyethyl cellulose, sodium salt of carboxymethyl cellulose, and ammonium salt of carboxymethyl cellulose, or a vinyl acetate polymer obtained by emulsion polymerization using co-polymeric surfactant, and
the inorganic acid of said inorganic acid amine salt is selected from boric acid, molybdenum acid or tungsten acid.
2. A lubricant composition for hot forming comprising: solid lubricant from 15 to 30% by mass; water-dispersible synthetic resin from 5 to 15% by mass; inorganic acid amine salt from 0.5 to 3% by mass; and water from 47 to 77% by mass, for 100% by mass of the total mass of the lubricant composition,
wherein said water-dispersible synthetic resin is a vinyl acetate polymer obtained by emulsion polymerization using protective colloid selected from a group consisting of hydroxyethyl cellulose, sodium salt of carboxymethyl cellulose, and ammonium salt of carboxymethyl cellulose, or a vinyl acetate polymer obtained by emulsion polymerization using co-polymeric surfactant, and
the inorganic acid of said inorganic acid amine salt is selected from boric acid, molybdenum acid or tungsten acid.
3. A lubricant composition for hot forming according to claim 1 , wherein the amine salt of said inorganic acid is a boric amine salt.
4. A lubricant composition for hot forming according to claim 1 , in a water resistance test, peeling below 15% is shown at the temperature of 80° C., and in water washability test, peeling of 85% or more is shown at the temperature of 40° C.
5. A method for producing seamless pipe or tube comprising the steps of: applying of the lubricant composition for hot forming as claimed in claim 1 to a mandrel bar, and continuously rolling a pipe or tube by utilizing this mandrel bar.
6. A lubricant composition for hot forming according to claim 2 , wherein the amine salt of said inorganic acid is a boric amine salt.
7. A lubricant composition for hot forming according to claim 2 , in a water resistance test, peeling below 15% is shown at the temperature of 80° C., and in water washability test, peeling of 85% or more is shown at the temperature of 40° C.
8. A method for producing seamless pipe or tube comprising the steps of: applying of the lubricant composition for hot forming as claimed in claim 2 to a mandrel bar, and continuously rolling a pipe or tube by utilizing this mandrel bar.