Polyamide resin composition
The present invention relates to such a polyamide resin composition that is suitably used as a material of a gasoline tank and a material of a molded article, such as a hollow molded container including a beverage bottle, a film and a sheet. A polyamide resin that is good in heat stability upon molding and suffers less increase in filter back pressure is provided by regulating a polyamide resin composition to have a phosphorus content of from 30 to 200 ppm (excluding 200 ppm), and a sodium content/phosphorus content ratio (molar ratio) of from 3 to 7 (excluding 3 and 7) or regulating it to have a phosphorus content less than 30 ppm and an alkali metal content less than 45 ppm.
1. A polyamide resin composition comprising m-xylylenediamine (MXDA) as a diamine component and adipic acid (AA) as a dicarboxylic acid component, wherein the polyamide resin composition has:
a content of phosphorus atoms (P) and sodium atoms (Na) satisfying the following equations (3) and (4):
30≦P≦190 ppm (3)
3.5≦Na/P (molar ratio)<7.0 (4)
and
a back pressure increasing coefficient K* satisfying the following equation (1):
0<K*≦14 (1)
wherein K* represents a back pressure increasing coefficient expressed by the following equation:
K*=[ΔP (MPa)/ T (hr)]/[ Q (kg/hr)/ S (cm 2 )]
wherein ΔP (MPa) represents a difference between an initial secondary pressure of a gear pump and a secondary pressure thereof after a lapse of T (hr); T (hr) represents a period of time of filtering the polyamide resin composition with a filter; Q (kg/hr) represents a discharge amount of the polyamide resin composition; S (cm 2 ) represents a filtering area of the filter; and the filter has a filtering diameter of 20 μm.
2. The polyamide resin composition described in claim 1 , wherein the polyamide resin composition has a back pressure increasing coefficient K* satisfying the following equation (2):
0<K*<5 (2)
wherein K* represents a back pressure increasing coefficient expressed by the following equation:
K*=[ΔP (MPa)/ T (hr)]/[ Q (kg/hr)/ S (cm 2 )]
wherein ΔP (MPa) represents a difference between an initial secondary pressure of a gear pump and a secondary pressure thereof after a lapse of T (hr); T (hr) represents a period of time of filtering the polyamide resin composition with a filter; Q (kg/hr) represents a discharge amount of the polyamide resin composition; S (cm 2 ) represents a filtering area of the filter; and the filter has a filtering diameter of 20 μm.
3. The polyamide resin composition as described in claim 1 , wherein the polyamide resin composition has a Co-b value satisfying the following equation (5):
−3<Co-b<10 (5).
4. The polyamide resin composition of claim 1 , wherein the back pressure increasing coefficient K* is 10 or less.
5. The polyamide resin composition of claim 1 , wherein the back pressure increasing coefficient K* is 8 or less.
6. The polyamide resin composition of claim 1 , wherein the back pressure increasing coefficient K* is 7 or less.
7. The polyamide resin composition of claim 1 , wherein the back pressure increasing coefficient K* is 6 or less.
8. The polyamide resin composition of claim 1 , wherein the back pressure increasing coefficient K* is 5 or less.