Process for making high-performance polyethylene multifilament yarn
The invention relates to a process for making high-performance polyethylene multi-filament yarn comprising the steps of a) making a solution of ultra-high molar mass polyethylene in a solvent; b) spinning of the solution through a spinplate containing at least 5 spinholes into an air-gap to form fluid filaments, while applying a draw ratio DR fluid ; c) cooling the fluid filaments to form solvent-containing gel filaments; d) removing at least partly the solvent from the filaments; and e) drawing the filaments in at least one step before, during and/or after said solvent removing, while applying a draw ratio DR solid of at least 4, wherein in step b) each spinhole comprises a contraction zone of specific dimension and a downstream zone of diameter D n and length D n with L n /D n of from 0 to at most 25, to result in a draw ratio DR fluid =DR sp *DR ag of at least 150, wherein DR sp is the draw ratio in the spinholes and DR ag is the draw ratio in the air-gap, with DR sp being greater than 1 and DR ag at least 1. The invention further relates to a high-performance polyethylene multifilament yarn, and to semi-finished or end-use products containing said yarn, especially to ropes and ballistic-resistant composites.
1. High-performance polyethylene multifilament yarn comprising n filaments and having a tensile strength of at least f *(n −0.065 ) GPa, wherein factor f is at least 5.8 and n is at least 5, and wherein the filaments are made from linear ultra-high molar mass polyethylene of IV 8-40 dl/g as measured on solutions in decalin at 135° C.
2. High-performance polyethylene multifilament yarn according to claim 1 wherein f has a value from 6.0 to 10.
3. High-performance polyethylene multifilament yarn according to claim 1 , showing a non-reversible peak, as measured by temperature-modulated differential scanning calorimetry, with a maximum at about 152° C. and having an enthalpy of at least 35 J/g.
4. High-performance polyethylene multifilament yarn according to claim 1 , having a creep rate as determined on yarn at 70° C. with a load of 600 MPa of at most 5* 10 −6 s −1 .
5. High-performance polyethylene multifilament yarn according to claim 1 , containing at least 200 filaments.
6. High-performance polyethylene multifilament yarn according to claim 1 , wherein the filaments are solution spun, and wherein the filaments contain less than 150 ppm of residual spinning solvent of a type having a boiling point at atmospheric conditions of less than 275° C.
7. Semi-finished and end-use articles containing the high-performance polyethylene multi-filament yarn according to claim 1 .