Method for producing discharge lamps
A process for producing a discharge lamp, includes the following process steps: providing a discharge vessel, producing a paste for a functional layer from the components: pulverulent base material, polyalkylene carbonate as binder and solvent, forming the functional layer by applying the paste to at least part of the wall of the discharge vessel. The type of base material depends on the type of functional layer, such as for example phosphor layer, reflective layer or soldering glass layer. The use of a polyalkylene carbonate as binder allows the binder to be removed without leaving any residues at relatively low binder-removal temperatures and therefore allows efficient lamps to be produced.
1 . A process for producing a discharge lamp, comprising the following process steps:
a. providing a discharge vessel,
b. producing a paste for a functional layer from the following components:
pulverulent base material,
polyalkylene carbonate as binder,
solvent,
c. forming the functional layer by applying the paste to at least part of the wall of the discharge vessel,
d. if necessary, repeating steps b and c if more than one functional layer is intended.
2 . The process as claimed in claim 1 , in which the pulverulent base material comprises a phosphor or phosphor mixture in order to form a phosphor layer ( 3 ) as functional layer.
3 . The process as claimed in claim 2 , in which the phosphor or the phosphor mixture comprises one or more components selected from the group consisting of BaMgAl 10 O 17 :Eu, LaPO 4 :(TB, Ce), (Gd, Y)BO 3 :Eu.
4 . The process as claimed in claim 1 , in which the pulverulent base material consists of a reflective substance or reflective substance mixture, in order to form a reflective layer ( 4 ) as functional layer.
5 . The process as claimed in claim 4 , in which the reflective substance or the reflective substance mixture comprises A 1 2 O 3 and/or TiO 2 .
6 . The process as claimed in claim 1 , in which the pulverulent base material consists of a soldering glass or soldering glass mixture, in order to form a soldering glass layer ( 5 ) as functional layer.
7 . The process as claimed in claim 6 , in which the soldering glass or soldering glass mixture comprises Pb—B—Si—O.
8 . The process as claimed in claim 1 , in which the solvent comprises ethyl acetate.
9 . The process as claimed in claim 1 , in which the solvent comprises propylene glycol diacetate.
10 . The process as claimed in claim 1 , in which the binder polyalkylene carbonate forms approx. 0.5 to 2% by weight, in particular 1 to 1.5% by weight.
11 . The process as claimed in claim 1 , in which the polyallkylene carbonate used as binder is polypropylene carbonate.
12 . The process as claimed in claim 1 , in which the paste is applied by spraying, dispensing or screen printing.
13 . The process as claimed in claim 1 , in which the discharge lamp is designed as a flat discharge lamp and the discharge vessel comprises two substantially planar plates ( 1 , 2 ) which are joined to one another in a gastight manner.
14 . The process as claimed in claim 1 , in which the discharge lamp is designed for operation based on dielectric barrier discharges.
15 . The process as claimed in claim 2 , in which the pulverulent base material consists of a reflective substance or reflective substance mixture, in order to form a reflective layer ( 4 ) as functional layer.
16 . The process as claimed in claim 3 , in which the pulverulent base material consists of a reflective substance or reflective substance mixture, in order to form a reflective layer ( 4 ) as functional layer.