The present invention relates to moldable composite articles, and particularly to a molded nonwoven fibrous article, and specifically to an automobile headliner that has improved physical properties at low weight. There is a need to minimize the weight of the headliner and the critical parameter is minimum sag. For a molded non-needlepunched batt in the weight range of 1000 to 1200 grams per square meter (gsm), the sag at 91° C. must be less than 10 mm, when cantilevering a distance of 28 cm. The stiffness, strength and toughness of the batt should be greater than 2 N/mm, 17N and 70% respectively. In the first embodiment, the thermoplastic binder is a bicomponent fiber with an adhesion promoted polyolefin sheath and a polyester core. In the second embodiment, the matrix fiber is a synthetic fiber with a modulus greater than 10 cN/tex. In the third embodiment the matrix fiber is a natural fiber. In the fourth embodiment the bicomponent fiber contains a filler such as carbon black or titanium dioxide.
1 ) A nonwoven batt suitable for use in a molded article comprising: a blend of synthetic and/or natural fibers, and bicomponent fiber, said bicomponent fiber having a low melting portion that is adhesion promoted polyolefin, wherein the sag of a molded non-needlepunched batt, at 91° C. is less than 10 mm measured when the weight range of the batt is 1000 to 1200 grams per square meter, cantilevering a distance of 28 cm.
2 ) The batt of claim 1 , wherein said synthetic fiber has a modulus of at least 10 cN/tex.
3 ) The batt of claim 2 , wherein said synthetic fiber is selected from the class of polyester or polyamide.
4 ) The batt of claim 1 , wherein said adhesion promoted polyolefin is maleic anhydride grafted polyethylene.
5 ) The batt of claim 1 , wherein said natural fiber is selected from the class of wood pulp, jute, kenaf, wool, cotton or flax.
6 ) The batt of claim 1 , wherein said synthetic and/or natural fibers comprise from about 25-45 wt % of said batt and said bicomponent fiber comprise from about 55-75 wt % of said batt.
7 ) The batt of claim 1 , wherein said low melting component of said bicomponent fiber contains filler.
8 ) The batt of claim 7 , wherein said filler is carbon black or titanium dioxide.
9 ) The batt of claim 7 , wherein said filler is present in an amount of from about 0.1 to about 0.3 weight % of said low melting portion, and said low melting portion is about 50 weight % of said bicomponent fiber.
10 ) A nonwoven batt suitable for use in a molded article comprising: a non-needlepunched blend of synthetic polyester and/or natural fibers comprising from about 25-45 wt % of said batt, and bicomponent fiber comprising from about 55-75 wt % of said batt, said bicomponent fiber having a low melting portion that is adhesion promoted polyolefin and said low melting portion is about 50 weight % of said bicomponent fiber.
11 ) The batt of claim 10 , wherein said polyester fiber has a modulus of at least 10 cN/tex.
12 ) The batt of claim 10 , wherein said adhesion promoted polyolefin is maleic anhydride grafted polyethylene.
13 ) The batt of claim 10 , wherein the sag of a molded batt at 91° C. is less than 10 mm measured when the weight range of the batt is 1000 to 1200 grams per square meter, cantilevering a distance of 28 cm.
14 ) A molded article comprising a blend of synthetic and/or natural fibers, and bicomponent fiber, said bicomponent fiber having a low melt portion that is adhesion promoted polyolefin, wherein the sag of the said molded article, non-needlepunched, at 91° C. is less than 10 mm measured when the weight range of the batt is 1000 to 1200 grams per square meter, cantilevering a distance of 28 cm.
15 ) The molded article of claim 14 , wherein synthetic and/or natural fibers comprise from about 25-45 wt % of said blend and said bicomponent fiber comprise from about 55-75 wt % of said blend.
16 ) The molded article of claim 14 , wherein said synthetic fiber is selected from the class of polyester or polyamide.
17 ) The molded article of claim 14 , wherein said adhesion promoted polyolefin is maleic anhydride grafted polyethylene.
18 ) The molded article of claim 14 , wherein said natural fiber is selected from the class of wood pulp, jute, kenaf, wool, cotton or flax.
19 ) The molded article of claim 14 , wherein said synthetic fiber has a modulus of at least 10 cN/tex.
20 ) The molded article of claim 14 , wherein said low melting component of said bicomponent fiber contains filler.
21 ) The molded article of claim 20 , wherein said filler is carbon black or titanium dioxide.
22 ) The molded article of claim 20 , wherein said filler is present in an amount of from about 0.1 to about 0.3 weight % of said low melting portion, and said low melting portion is about 50 weight % of said bicomponent fiber.
23 ) A molded article suitable for use in a vehicle headliner comprising: a blend of synthetic polyester and/or natural fibers comprising from about 25-45 wt % of said blend, and bicomponent fiber comprising from about 55-75 wt % of said blend, said bicomponent fiber having a low melting portion that is adhesion promoted polyolefin and said low melting portion is about 50 weight % of said bicomponent fiber.
24 ) The molded article of claim 23 , wherein said polyester fiber has a modulus of at least 10 cN/tex.
25 ) The molded article of claim 23 , wherein the sag of the said molded article, non-needlepunched, at 91 ° C. is less than 10 mm measured when the weight range of the batt is 1000 to 1200 grams per square meter, cantilevering a distance of 28 cm.
26 ) The batt of claim 7 , wherein said filler is graphite, talc, metal carbonates and sulfates, other inorganic particles, metal benzoates and stearates, benzoic acid, dibenzylidene sorbitol derivates, titanium dioxide, carbon black, or a mixture of two or more of these.