Steel plate or steel pipe with small occurrence of Bauschinger effect and methods of production of same
View Patent ↗The present invention provides steel plate or steel pipe with small occurrence of the Bauschinger effect and methods of production of the same, particularly steel pipe used for steel pipe for oil wells or line pipe with a small drop in the compression strength in the circumferential direction due to the Bauschinger effect when expanded and methods of production of the same, that is steel plate or steel pipe with small occurrence of the Bauschinger effect characterized by having a dual-phase structure substantially comprising a ferrite structure and fine martensite which is dispersed in the ferrite structure. Further, this steel plate or steel pipe contains, by mass %, C: 0.03 to 0.30%, Si: 0.01 to 0.8%, Mn: 0.3 to 2.5%, P: 0.03% or less, S: 0.01% or less, Al: 0.001 to 0.01%, and N: 0.01% or less and a balance of iron and unavoidable impurities.
1. A steel pipe formed from a plate of a steel base material, wherein the steel base material comprises, by mass %, C: 0.03 to 0.30%, Si: 0.01 to 0.8%, Mn: 0.3 to 2.5%, P: 0.03% or less, S: 0.01% or less, Al: 0.001 to 0.1%, N: 0.01% or less, and a balance of iron and unavoidable impurities,
wherein the steel pipe is heated in the austenite-ferrite dual-phase temperature region and is then quenched,
wherein the heating and the quenching are conducted after the plate of the steel base material is shaped into the steel pipe, and
wherein the steel pipe has:
a dual-phase structure substantially comprising a ferrite structure and fine martensite dispersed at the ferrite grain boundaries, and
a ratio of the proportional limit of the compression stress-strain curve in the circumferential direction before and after expansion of at least 0.7,
wherein the fine martensite has grains of a long axis of 10 μm or less and said fine martensite has an area ratio of 10 to 30%.
2. The steel pipe as set forth in claim 1 , wherein the pipe is heated at a temperature range of 760 to 830° C.
3. The steel pipe as set forth in claim 1 , further containing, by mass %, one or more of Nb: 0.1% or less, V: 0.3% or less, Mo: 0.5% or less, Ti: 0.1% or less, Cr: 1.0% or less, Ni: 1.0% or less, Cu: 1.0% or less, B: 0.003% or less, and Ca: 0.004% or less.
4. The steel pipe as set forth in claim 1 , further containing, by mass %, C: 0.03 to 0.10%, having a Charpy V-notch value in the transverse direction at −20° C. of 40 J or more, and wherein the ratio of the proportional limit of the compression stress-strain curve before and after being subjected to deformation is 0.7 or more.