Plastic optical fiber and method for manufacturing the same
View Patent ↗A preform ( 15 ) having a clad part of PVDF and a core part of PMMA is manufactured. The preform ( 15 ) is partially heated in a heating furnace ( 74 ) of 240° C. The preform ( 15 ) is subject to the melt-drawing process to form a plastic optical fiber ( 17 ). The drawing tension to the preform ( 15 ) is measured by use of a drawing tension measure device ( 76 ). Based on the measured value, a drawing roller pair ( 78 ) adjusts the drawing tension to be 3.8 MPa. The plastic optical fiber ( 17 ) is fed via a dancer roller ( 82 ) and rollers ( 84, 86 ) toward a bobbin ( 87 ) to wind the plastic optical fiber ( 17 ). A winding tension measure device ( 85 ) measures the winding tension to the POF ( 17 ). Based on the measured value, the dancer roller ( 82 ) changes its position to adjust the winding tension to be 2.5 MPa.
1. A method for manufacturing a plastic optical fiber, the method comprising the steps of:
(a) applying winding tension to the heated plastic optical fiber;
(b) winding the plastic optical fiber such that the plastic optical fiber just after the winding process has the shrinkage of 0.10% or smaller; and
(c) adjusting the winding tension by an adjustment tension that is different from the winding tension,
wherein the adjustment tension is 1.5 MPa to 7.0 MPa.
2. The method according to claim 1 , wherein the diameter of the plastic optical fiber is 1000μm or smaller.
3. The method according to claim 1 , wherein the winding tension is 0.5 MPa to 5.0 MPa.
4. The method according to claim 1 , wherein the heated plastic optical fiber is produced by melt-drawing a plastic optical fiber base material.
5. The method according to claim 1 , wherein the plastic optical fiber is wound around a winding member that comprises a bobbin body and a soft material wound around the bobbin body;
wherein the hardness of the soft material measured by type E Durometer is 10 to 70.
6. The method according to claim 1 , wherein the clad part of the plastic optical fiber is formed from fluorine resin.
7. The method according to claim 1 , wherein the core part of the plastic optical fiber is formed from acrylic resin.
8. The method according to claim 1 , wherein the core part of the plastic optical fiber has a refractive index profile in which the refractive index decreases from the center to the surface.
9. A method for manufacturing a plastic optical fiber, the method comprising the steps of:
(a) melting and drawing a plastic optical fiber base material to form a plastic optical fiber;
(b) applying winding tension to the plastic optical fiber;
(c) winding the plastic optical fiber such that the plastic optical fiber just after the winding process has the shrinkage of 0.10% or smaller; and
(d) adjusting the winding tension by an adjustment tension that is different from the winding tension,
wherein the adjustment tension is 1.5 MPa to 7.0 MPa.