Nanoscalar silicon particles in negative electrode materials for use in lithium-ion batteries
View Patent ↗The invention relates to an electrode material for a lithium ion battery which is distinguished by the fact that the electrode material comprises 5-85% by weight of nanoscale silicon particles which have a BET surface area of from 5 to 700 m 2 /g and a mean primary particle diameter of from 5 to 200 nm, 0-10% by weight of conductive carbon black, 5-80% by weight of graphite having a mean particle diameter of from 1 μm to 100 μm and 5-25% by weight of a binder, the proportions of the components summing to not more than 100% by weight, and to the use of the electrode material according to the invention for the production of lithium ion batteries, and to a lithium ion battery having a negative electrode which comprises the electrode material according to the invention.
1. An electrode material for lithium ion batteries, comprising
5-85% by weight of nanoscale silicon aggregate particles which have a BET surface area of from 5 to 700 m 2 /g and a mean primary particle diameter of from 5 to 200 nm,
0-10% by weight of conductive carbon black,
5-80% by weight of graphite having a mean particle diameter of from 1 μm to 100 μm and
5-25% by weight of a binder,
the proportions of the components summing to not more than 100% by weight.
2. The electrode material according to claim 1 , wherein said electrode material comprises
65-86.5% by weight of nanoscale silicon aggregate particles,
0.5-5% by weight of conductive carbon black,
8-20% by weight of graphite having a mean particle diameter of from 2 μm to 50 μm and
5-10% by weight of a binder.
3. The electrode material according to claim 1 , wherein said electrode material comprises
5-40% by weight of nanoscale silicon aggregate particles,
55-85% by weight of graphite having a mean particle diameter of from 2 μm to 50 μm and
5-10% by weight of a binder.
4. The electrode material according to claim 1 , wherein said nanoscale silicon aggregate particles are doped.
5. The electrode material according to claim 4 , wherein said nanoscale silicon aggregate particles comprise not more than 53% by weight of lithium as a doping component.
6. The electrode material according to claim 1 , wherein said nanoscale silicon aggregate particles have a BET surface area of from 6 to 140 m 2 /g.
7. A method of preparing a lithium ion battery comprising assembling with an electrode material according to claim 1 .
8. The method according to claim 7 , wherein said lithium ion battery comprises an electrolyte composition which comprises from 0.5 to 10% by weight of vinylene carbonate.
9. The method according to claim 7 , wherein said lithium ion battery comprises an electrolyte composition comprising at least one organic solvent and at least one alkali metal salt or alkaline earth metal salt.
10. The method according to claim 9 , wherein said organic solvent is at least one organic solvent selected from the group consisting of ethylene carbonate, dimethyl carbonate, ethyl methyl carbonate, diethyl carbonate, propylene carbonate, butylene carbonate, methyl propyl carbonate, butyl methyl carbonate and its isomers, 1,2 dimethoxyethane, tetrahydrofuran, 2 methyltetrahydrofuran, diethylene glycol dialkyl ester, dioxolane, propylene oxide, dimethyl sulfoxide, dimethylformamide, formamide, nitromethane, gamma-butyrolactone, alkyl esters of carboxylic acids and/or methyl lactate.
11. The method of using according to claim 9 , wherein said electrolyte composition comprises at least one alkali metal salt selected from the group consisting of LiPF 6 , LiClO 4 , LiAsF 6 , LiBF 4 , LiCF 3 SO 3 , LiN(CF 3 SO 2 ) 2 , LiN(SO 2 CF 2 CF 3 ) 2 , LiSbF 6 , LiAlCl 4 , LiGaCl 4 , LiCl, LiNO 3 , LiSCN, LiO 3 SCF 2 CF 3 , LiC 6 F 5 SO 3 , LiO 2 CCF 3 , LiFSO 3 , LiB(C 6 H 5 ) 4 , LiB(C 2 O 4 ) 2 , and/or lithium fluoroalkylphosphates.
12. The method of using according to claim 7 , wherein said lithium ion battery comprises an electrolyte composition in which the concentration of a conductive salt is from 0.5 mol/l to the solubility limit of the corresponding salt.
13. A lithium ion battery having a negative electrode which comprises an electrode material according to claim 1 .
14. The electrode material according to claim 1 , wherein a conductive carbon black is present in an amount of 0.5 to 4% by weight.
15. The electrode material according to claim 1 , wherein a conductive carbon black is present and has a mean particle size of from 20-60 nm.
16. The electrode material according to claim 1 , wherein a conductive carbon black is present and has a BET surface area of from 50 to 80 m 2 /g.
17. The electrode material according to claim 1 , wherein said graphite has a d 90 value of from 5 to 10 μm.
18. The electrode material according to claim 1 , wherein said graphite has a BET surface area of from 5 to 30 m 2 /g.