Use of tocopherol to scavenge acetaldehyde in polyethylene terephthalate containers
A polymeric compound is disclosed comprising polyethylene terephthalate and DL-alpha-Tocopherol. DL-alpha-Tocopherol serves as a scavanger for acetaldehyde in headspace of containers comprising polyethylene terephthalate.
1 . A compound, comprising:
(a) polyethylene terephthalate, and
(b) an acetaldehyde scavenger consisting essentially of DL-alpha-Tocopherol present in an amount ranging from about 5% to about 18% of the compound.
2 . The compound of claim 1 , further comprising colorant.
3 . The compound of claim 1 , wherein the DL-alpha-Tocopherol is present in an amount ranging from about 5% to about 16.7% of the compound.
4 . The compound of claim 1 , further comprising an additive selected from the group consisting of slip agents, antiblocking agents, antioxidants, ultraviolet light stabilizers, quenchers, plasticizers, mold release agents, lubricants, antistatic agents, fire retardants, fillers, and combinations thereof.
5 . The compound of claim 4 , wherein the filler comprises glass fibers, talc, chalk, clay, or combinations thereof.
6 . The compound of claim 4 , wherein the additive is included in the compound in an amount from 0 to about 40 weight percent.
7 . The compound of claim 2 , wherein the colorant is either
(a) an inorganic pigment selected from the group consisting of titanium dioxide, iron oxide, chromium oxide, lead chromate, carbon black, silica, talc, china clay, metallic oxides, silicates, chromates, and combinations thereof, or
(b) an organic pigment selected from the group consisting of phthalocyanine blue, phthalocyanine green, carbazole violet, anthrapyrimidine yellow, flavanthrone yellow, isoindoline yellow, indanthrone blue, quinacridone violet, perylene reds, diazo red, and combinations thereof.
8 . The compound of claim 7 , wherein the amount of colorant can range from none at all to about 4.0 weight percent.
9 . A container made from the compound of claim 1 .
10 . The container of claim 9 , further comprising colorant.
11 . The container of claim 9 , wherein the DL-alpha-Tocopherol is present in an amount ranging from about 5% to about 16.7% of the compound.
12 . The container of claim 9 , further comprising an additive selected from the group consisting of slip agents, antiblocking agents, antioxidants, ultraviolet light stabilizers, quenchers, plasticizers, mold release agents, lubricants, antistatic agents, fire retardants, fillers, and combinations thereof.
13 . The container of claim 12 , wherein the filler comprises glass fibers, talc, chalk, clay, or combinations thereof.
14 . The container of claim 12 , wherein the additive is included in the compound in an amount from 0 to about 40 weight percent.
15 . The container of claim 10 , wherein the colorant is either
(a) an inorganic pigment selected from the group consisting of titanium dioxide, iron oxide, chromium oxide, lead chromate, carbon black, silica, talc, china clay, metallic oxides, silicates, chromates, and combinations thereof or
(b) an organic pigment selected from the group consisting of phthalocyanine blue, phthalocyanine green, carbazole violet, anthrapyrimidine yellow, flavanthrone yellow, isoindoline yellow, indanthrone blue, quinacridone violet perylene reds, diazo red, and combinations thereof.
16 . The container of claim 10 , wherein the DL-alpha-Tocopherol is present in an amount ranging from about 5% to about 16.7% of the compound.
17 . The container of claim 10 , further comprising an additive selected from the group consisting of slip agents, antiblocking agents, antioxidants, ultraviolet light stabilizers, quenchers, plasticizers, mold release agents, lubricants, antistatic agents, fire retardants, fillers, and combinations thereof.
18 . The container of claim 17 , wherein the filler comprises glass fibers, talc, chalk, clay, or combinations thereof.
19 . The container of claim 17 , wherein the additive is included in the compound in an amount from 0 to about 40 weight percent.