Warm molding raw material powder and warm molding method
View Patent ↗A hydroxy fatty acid salt having an average particle diameter of from 5 μm to 100 μm with a composition of from 0.3 wt % to 2 wt %, and more preferably, from 0.5 wt % to 2 wt % is added to a raw material powder in powder metallurgy, and worm molding is performed. In addition, a hydroxy fatty acid salt having an average particle diameter of 50 μm or less is attached on a mold in advance, and after that, the warm molding is performed. As a hydroxy fatty acid salt, 12-hydroxy lithium stearate is suitably used.
1. A warm molding method comprising:
attaching a powder consisting of a hydroxyl fatty acid salt having an average particle diameter of 50 μm or less on a forming surface of a mold; and
using a warm molding raw material powder in powder metallurgy, the warm molding raw material powder comprising a lubricant which consists of a hydroxyl fatty acid salt having an average particle diameter of from 5 μm to 100 μm in a range of from 0.3 wt % to 2 wt %.
2. The warm molding method according to claim 1 , wherein the hydroxy fatty acid salt is a hydroxy fatty acid lithium.
3. The warm molding method according to claim 2 , wherein the hydroxy fatty acid lithium is hydroxy lithium stearate.
4. The warm molding method according to claim 3 , wherein the hydroxy lithium stearate is 12-hydroxy lithium stearate.
5. The warm molding method according to claim 1 , wherein the warm molding raw material powder is heated up to a temperature of 150 to 190° C.
6. The warm molding method according to claim 1 , wherein the hydroxy fatty acid salt is a hydroxy stearic acid salt.
7. The warm molding method according to claim 6 , wherein the hydroxy stearic acid salt is hydroxy lithium stearate.
8. The warm molding method according to claim 7 , wherein the hydroxy lithium stearate is 12-hydroxy lithium stearate.