View Patent ↗In the method for producing a magnetic recording medium having a nonmagnetic substrate coated with a magnetic coating material containing a ferromagnetic powder and a binder, the magnetic coating material contains a liquid A constituted by the ferromagnetic powder and a solvent, and a solution B of the binder, and the liquid A and the solution B are mixed together by applying an ultrasonic wave thereto, and are thereafter subjected to dispersion processing. Thereby, coagulated particles of the ferromagnetic powder can be dispersed and the coagulation of the ferromagnetic powder can be prevented, thus making it possible to obtain a liquid of ferromagnetic powder with uniform adsorption of the binder. As a result, a magnetic coating material suitable for a low-noise high-density coating-type magnetic recording medium is obtained.
1. A method for producing a magnetic recording medium having a nonmagnetic substrate coated with a magnetic coating material containing a ferromagnetic powder and a binder, comprising:
preparing a liquid A constituted by a ferromagnetic powder and a solvent;
preparing a solution B of a binder;
mixing the liquid A and the solution B together in a liquid-liquid state by applying an ultrasonic wave thereto, and thereafter subjecting the mixture to dispersion processing to obtain a magnetic coating material to achieve the binder uniformly absorbed on the surface of the substrate; and
coating a nonmagnetic substrate with the magnetic coating material whereby a lower noise and higher density coating is achieved by reducing secondary coagulation as compared to initial contact of binder and ferromagnetic material powder in a mixer.
2. The method as defined in claim 1 , wherein the ultrasonic wave is applied within one second after the liquid A and the solution B are mixed together.
3. The method as defined in claim 1 , wherein the liquid A is subjected to dispersion processing by applying the ultrasonic wave thereto before the liquid A and the solution B are mixed together.
4. The method as defined in claim 1 , wherein the ferromagnetic powder is a needle particle with a major axis length of 10 to 100 nm.
5. The method as defined in claim 1 , wherein the ferromagnetic powder is a plate particle with a plate diameter of 10 to 50 nm.
6. A method for producing a magnetic recording medium having a nonmagnetic substrate coated with a magnetic coating material containing a ferromagnetic powder and a binder, comprising:
preparing a liquid A constituted by a ferromagnetic powder and a solvent;
preparing a solution B of a binder;
subjecting the liquid A to dispersion processing by applying an ultrasonic wave thereto, and thereafter mixing the liquid A and the solution B together in a liquid-liquid state to obtain a magnetic coating material to achieve the binder uniformly absorbed on the surface of the substrate; and
coating a non-magnetic substrate with the magnetic coating material whereby a lower noise and higher density coating is achieve by reducing secondary coagulation as compared to initial contact of binder and ferromagnetic material powder in a mixer.
7. The method as defined in claim 6 , wherein the ferromagnetic powder is a needle particle with a major axis length of 10 to 100 nm.
8. The method as defined in claim 6 , wherein the ferromagnetic powder is a plate particle with a plate diameter of 10 to 50 nm.