Cold in-place recycling of bituminous material
View Patent ↗A method of reconstructing a road is provided. This method includes taking representative cores of the road, analyzing the cores, selecting a substantially solvent-free emulsion based on climate history, mixing the emulsion and reclaimed asphalt pavement particles to form an asphalt emulsion mix, testing the asphalt emulsion mix for performance using a raveling test, a thermal cracking prediction test by an indirect tensile testing, a moisture susceptibility test utilizing vacuum saturation, and a dry Marshall stability test. It also includes designing a CIR layer based on this test data. It further includes grinding off a layer of the existing asphalt road leaving at least about an inch, adding an emulsion to the reclaimed asphalt pavement particles, applying the designed cold in-place recycling layer to the road, and compacting it.
1. A method of selecting an asphalt emulsion mixture to be used for reconstructing a paved road, comprising:
providing reclaimed asphalt pavement particles;
selecting an emulsion;
mixing said emulsion and said reclaimed asphalt pavement particles to form a proposed asphalt emulsion mixture;
testing said proposed asphalt emulsion mixture for performance using a raveling test and a moisture susceptibility test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing said proposed asphalt emulsion mixture for performance.
2. The method of claim 1 , further comprising:
testing said proposed asphalt emulsion mixture for performance using a stability test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing said proposed asphalt emulsion mixture for performance.
3. The method of claim 2 , further comprising:
testing modulus of said proposed asphalt emulsion mixture; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing modulus of said proposed asphalt emulsion mixture.
4. The method of claim 3 , wherein resilient modulus is tested.
5. The method of claim 1 , further comprising:
testing modulus of said proposed asphalt emulsion mixture; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing modulus of said proposed asphalt emulsion mixture.
6. The method of claim 5 , wherein resilient modulus is tested.
7. The method of claim 1 , further comprising:
testing said proposed asphalt emulsion mixture for performance using a thermal cracking test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing thermal cracking of said proposed asphalt emulsion mixture.
8. The method of claim 1 , further comprising:
testing said proposed asphalt emulsion mixture for performance using a thermal cracking test and a stability test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing thermal cracking and stability of said proposed asphalt emulsion mixture.
9. The method of claim 1 , wherein said selected asphalt emulsion mixture comprises a cationic emulsifier.
10. The method of claim 1 , further comprising:
taking samples of said road; and
using said samples to make said reclaimed asphalt pavement particles.
11. The method of claim 10 , further comprising:
inspecting said samples to determine the composition of layers in said samples, the thickness of said layers, and variations between samples.
12. The method of claim 10 , wherein said samples are crushed to form reclaimed asphalt pavement particles.
13. The method of claim 10 , wherein said samples are representative of variations in the road.
14. The method of claim 1 , wherein at least two different proposed asphalt emulsion mixtures are formulated and tested for performance before said asphalt emulsion mixture to be used for reconstruction said paved road is selected.
15. The method of claim 1 , wherein said selected asphalt emulsion mixture ravels no more than about 2% by weight after curing for at least about 4 hours.
16. The method of claim 7 , wherein said selected asphalt emulsion mixture has a critical cracking temperature that is at least as low as the possible coldest temperature of said road with 98% reliability.
17. The method of claim 1 , wherein said selected asphalt emulsion mixture has a retained strength, as determined by a moisture susceptibility test, of at least about 70%.
18. A method of reconstructing a paved road, comprising:
forming a proposed asphalt emulsion mixture from an emulsion and reclaimed asphalt pavement particles;
testing said proposed asphalt emulsion mixture for performance using a raveling test and a moisture susceptibility test; and
selecting an asphalt emulsion mixture to be used for reconstructing said paved road after testing said proposed asphalt emulsion mixture for performance;
removing pavement from said road to form reclaimed asphalt pavement particles, leaving at least about an inch of said pavement on said road;
mixing said reclaimed asphalt pavement particles from said road with an emulsion to form said selected asphalt emulsion mixture; and
applying said selected asphalt emulsion mixture to said partially reclaimed road so as to form a cold in-place recycling layer on said road.
19. The method of claim 18 , further comprising:
inspecting said road to determine if said road is thick enough to leave at least about an inch base of pavement after removing pavement;
determining if said road has a structurally sound base; and
determining if said road has good drainage.
20. The method of claim 18 , further comprising;
applying to said cold in-place recycling layer a wearing surface selected from the group consisting of a cold, hot, or warm mix overlay, a seal coat, a chip seal, a fog seal.
21. The product of the process of claim 18 .
22. A method of selecting an asphalt emulsion mixture to be used for reconstructing a paved road, comprising:
providing reclaimed asphalt pavement particles;
selecting an emulsion;
mixing said emulsion and said reclaimed asphalt pavement particles to form a proposed asphalt emulsion mixture;
testing said proposed asphalt emulsion mixture for performance using a raveling test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing said proposed asphalt emulsion mixture for performance.
23. The method of claim 22 , further comprising:
testing said proposed asphalt emulsion mixture for performance using a stability test; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing said proposed asphalt emulsion mixture for performance.
24. The method of claim 23 , further comprising:
testing modulus of said proposed asphalt emulsion mixture; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing modulus of said proposed asphalt emulsion mixture.
25. The method of claim 24 , wherein resilient modulus is tested.
26. The method of claim 22 , further comprising:
testing modulus of said proposed asphalt emulsion mixture; and
selecting said asphalt emulsion mixture to be used for reconstructing said paved road after testing modulus of said proposed asphalt emulsion mixture.
27. The method of claim 26 , wherein resilient modulus is tested.