Process for preparing low-monomer-content TDI trimers
View Patent ↗The invention relates to a novel process for preparing low-monomer-content trimers based on 2,4- and 2,6-diisocyanatotoluene (TDI) and to the use thereof in coatings. The trimers are produced from a mixture of from 20 to 80% by weight of diisocyanate component containing at least 80% by weight of 2,4- and/or 2,6-diisocyanatotoluene and from 20 to 80% by weight of solvents and/or diluents and also phenolic catalysts containing dialkylaminomethyl groups.
1. Process for preparing solvent-containing and/or diluent-containing polyisocyanates based on 2,4- and/or 2,6-diisocyanato-toluene which contain isocyanurate groups and <0.1% by weight of monomeric disocyanate comprising
a) carrying out a catalytic trimerization of a diisocyanate component in the presence of a solvent component and a catalyst component; combined to form a mixture,
wherein the mixture comprises from 20 to 80% by weight diisocyanate component,
wherein the dilsocyanate component contains a mixture of 2,4-diisocyanatotoluene and 2,6-diisocyanatotoluen at a weight ratio of from 3:2 to 9:1,
wherein the mixture comprises from 20 to 80% by weight of solvents and/or diluents,
wherein the mixture comprises phenolic catalysts contaning dialkylaminomethyl groups, and
wherein the catalytic trimerization is carried out at a temperature from 70°C. and 120°C. in the absence of aliphatic hydroxyl groups and urethane groups, and
b) ending the reaction subsequently, by stopping with catalyst poisons.
2. Process according to claim 1 , wherein catalysts are used whose dilialkylaminomethyl groups (alkyl=C 1 to C 3 chain) and phenolic OH groups are positioned in one molecule.
3. Process according to claim 1 , wherein catalysts are used which are obtained as Mannich bases based upon phenol, p-isononylphenol or bisphenol A by reaction with dimethylamine end formaldehyde.
4. Process for preparing solvent-containing and/or diluent-containing polylisoyanates based on 2,4-diisocyanatotoluene which contain isocyanurate groups and <0.1% by weight of monomeric diisocyanate comprising
a) cariying out a catalytic trimerization of a diisocyanate component in the presence of a solvent component and a catalyst component; combined to form a mixture,
wherein the mixture comprises from 20 to 80% by weight diisocyanate component,
wherein 2,4-diisocyanatotoluene is used as starting diisocyanate, wherein the mixture comprises from 20 to 80% by weight of solvents and/or diluents,
wherein the mixture comprises phenolic catalysts containing dialkylaminomethyl groups, and
wherein the catalytic trimerizatlon is carried out at a temperature from 70 C. and 120 C. in the absence of aliphatic hydroxyl groups and urethane groups, and ending the reaction subsequently, by stopping with catalyst poisons.
5. Method for preparing polyurethane paints, coatings, adhesives, printing inks, sealants and polyurethane moldings, comprising adding polyisocyanates containing isocyanate groups made according to the process of claim 1 to a formulation.