Continuous in-line process for making ink-jet recording media comprising a radiation-cured coating layer
View Patent ↗Ink-jet recording media and continuous in-line process for manufacturing such media are provided. The media can be printed with ink-jet printers to form images having good color density, brilliance, and resolution. The ink-jet recording media include a paper substrate coated on one surface with a radiation-curable composition and an ink-receptive composition. The back surface of the paper may be coated with a polymeric coating to reduce curl and improve dimensional stability. The media have a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and preferably have a surface gloss of at least 70.
1. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
b) irradiating the radiation-curable coating to form a freshly irradiated coating that undergoes a curing process, and
c) applying an ink-receptive coating over the freshly irradiated coating to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss less than 20.
2. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
b) irradiating the radiation-curable coating with ultraviolet light to form a freshly irradiated coating that undergoes a curing process, and
c) applying an ink-receptive coating over the freshly irradiated coating to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss of at least 70.
3. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
b) irradiating the radiation-curable coating to form a freshly irradiated coating that undergoes a curing process,
c) treating the irradiated coating with a corona discharge, and
d) applying an ink-receptive coating over the freshly irradiated coating to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss of at least 70.
4. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
b) irradiating the radiation-curable coating to form a freshly irradiated coating that undergoes a curing process,
c) applying a coating comprising adhesion promoters over the freshly irradiated coating and
d) applying an ink-receptive coating over the coating comprising adhesion promoters to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss of at least 70.
5. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
wherein the radiation-curable coating comprises a radiation-curable oligomer and photoinitiator,
b) irradiating the radiation-curable coating to form a freshly irradiated coating that undergoes a curing process, and
c) applying an ink-receptive coating over the freshly irradiated coating to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss of at least 70.
6. A continuous, in-line process for making an ink-jet recording medium, comprising the steps of:
a) applying a radiation-curable coating to a surface of a substrate material,
b) irradiating the radiation-curable coating to form a freshly irradiated coating that undergoes a curing process, and
c) applying an ink-receptive coating over the freshly irradiated coating to form an ink-jet recording medium having a water vapor transmission rate of no greater than 12 grams/100 square inches/24 hours and a surface gloss of at least 70, and further
wherein the ink-receptive coating comprises at least about 40% by weight water-soluble binder resin based on dry weight of the ink-receptive layer.
7. The process of claim 6 , wherein the water-soluble binder resin is selected from the group consisting of polyvinyl alcohols; poly(vinyl pyrrolidone); poly(2-ethyl-2-oxazolinc); methylcellulose; poly(ethylene oxide); and copolymers and mixtures thereof.