Tempered glass sheet, process and apparatus therefor
View Patent ↗A tempered glass sheet having in its front view a peripheral region including the peripheries, and a central region ( 9 ) occupying inside the peripheral region, wherein the average surface compressive stress in the central region ( 9 ) is larger than the average surface compressive stress in the peripheral region, is presented, whereby a tempered glass sheet having a thickness thinner than conventional ones can be provided.
1. A tempered glass sheet comprising a residual compressive stress layer formed at a surface of the glass sheet and a residual tensile stress layer formed inside the glass sheet to increase strength of the glass sheet by a balance of residual stresses in these layers,
wherein the tempered glass sheet has in its front view a peripheral region including its periphery and a central region occupying an inside of the peripheral region, and an average surface compressive stress in the central region is larger than an average surface compressive stress in the peripheral region, and
wherein the average surface compressive stress is at least 90 MPa in the peripheral region of the tempered glass sheet.
2. The tempered glass sheet according to claim 1 , wherein a thickness of the tempered glass sheet is at most 2.8 mm, the average surface compressive stress in the central region is at least 100 MPa, and the average surface compressive stress in the peripheral region is at least 90 MPa.
3. The tempered glass sheet according to claim 1 ,
wherein a border between the central region and the peripheral region is defined by lines connecting points where tips of cracks propagating from a gravity point towards the peripheral region when the tempered glass sheet is fragmented at the gravity point, meet elastic waves generated at a same time with the cracks, propagated at a speed of 1.7 to 2.3 times as much as a speed of the cracks and reflected regularly at the periphery of the tempered glass sheet.
4. The tempered glass sheet according to claim 3 , wherein the average surface compressive stress in the central region is from 8 to 47% larger than the average surface compressive stress in the peripheral region.
5. The tempered glass sheet according to claim 1 , wherein the average surface compressive stress in the central region is from 8 to 47% larger than the average surface compressive stress in the peripheral region.
6. The tempered glass sheet according to claim 5 ,
wherein a thickness of the tempered glass sheet is at most 2.8 mm, the average surface compressive stress in the central region is at least 100 MPa, and the average surface compressive stress in the peripheral region is at least 90 MPa.
7. A tempered glass sheet comprising a residual compressive stress layer formed at a surface of the glass sheet and a residual tensile stress layer formed inside the glass sheet to increase strength of the glass sheet by a balance of residual stresses in these layers,
wherein the tempered glass sheet has in its front view a peripheral region including its periphery and a central region occupying an inside of the peripheral region, and an average surface compressive stress in the central region is larger than an average surface compressive stress in the peripheral region, and
wherein a thickness of the tempered glass sheet is at most 2.8 mm, the average surface compressive stress in the central region is at least 100 MPa, and the average surface compressive stress in the peripheral region is at least 90 MPa.
8. The tempered glass sheet according to claim 7 , wherein the average surface compressive stress in the central region is from 8 to 47% larger than the average surface compressive stress in the peripheral region.
9. The tempered glass sheet according to claim 7 ,
wherein a border between the central region and the peripheral region is defined by lines connecting points where tips of cracks propagating from a gravity point towards the peripheral region when the tempered glass sheet is fragmented at the gravity point, meet elastic waves generated at a same time with the cracks, propagated at a speed of 1.7 to 2.3 times as much as a speed of the cracks and reflected regularly at the periphery of the tempered glass sheet.
10. The tempered glass sheet according to claim 9 , wherein the average surface compressive stress in the central region is from 8 to 47% larger than the average surface compressive stress in the peripheral region.