Multilayered golf ball and composition
View Patent ↗A multilayer golf ball formed of a core, a cover layer and an optional intermediate layer disposed between the core and cover, wherein at least one layer includes a composition including a diisocyanate, a polyol or amine-terminated compound, and a curing agent, wherein the curing agent includes a diol or secondary diamine.
1. A golf ball comprising:
a core;
a layer disposed about the core having a hardness of about 30 Shore D or greater, a flexural modulus of about 1,000 psi to about 80,000 psi, and a thickness of about 0.01 inches to about 0.100 inches, wherein the layer is formed from a thermoplastic composition comprising p-phenylene diisocyanate and at least one hydroxy-terminated curing agent selected from the group consisting of poly(phthalate carbonate)glycol, poly(hexamethylene carbonate)glycol, polycarbonate polyols containing bisphenol A, and mixtures thereof; and
a cover having a hardness of about 20 Shore D or greater, a flexural modulus of about 1,000 psi to about 30,000 psi, and a thickness of about 0.01 inches to about 0.05 inches, wherein the cover is formed from a thermoset material.
2. The golf ball of claim 1 , wherein the core comprises a center and an outer core layer, and wherein the center has a diameter of about 0.5 inches to about 1.3 inches.
3. The golf ball of claim 1 , wherein the thermoplastic composition further comprises a hydroxy-terminated curing agent selected from the group consisting of polyethylene propylene glycol, polytetramethylene ether glycol, polyoxypropylene glycol, ethylene oxide capped poly(oxypropylene)glycol, and mixtures thereof.
4. The golf ball of claim 1 , wherein the thermoplastic composition further comprises a hydroxy-terminated curing agent selected from the group consisting of 1,6-hexanediol-initiated polycaprolactone, diethylene glycol initiated polycaprolactone, trimethylol propane initiated polycaprolactone, neopentyl glycol initiated polycaprolactone, 1,4-butanediol-initiated polycaprolactone, polytetramethylene ether glycol initiated polycaprolactone, and mixtures thereof.
5. The golf ball of claim 1 , wherein the thermoset material comprises polyurethane, polyurea, or combinations thereof.
6. The golf ball of claim 1 , wherein the core has a diameter of about 1.55 inches or greater.
7. The golf ball of claim 1 , wherein the cover has a thickness of about 0.025 inches to about 0.04 inches.
8. The golf ball of claim 1 , wherein the layer has a thickness of about 0.01 to about 0.045 inches.
9. The golf ball of claim 1 , wherein the layer has a hardness of about 50 to about 75 Shore D.
10. The golf ball of claim 1 , wherein the cover has a hardness of about 35 Shore D to about 55 Shore D.
11. A golf ball comprising:
a core;
a layer disposed about the core having a hardness of about 30 Shore D or greater, a flexural modulus of about 1,000 psi to about 80,000 psi, and a thickness of about 0.01 inches to about 0.100 inches, wherein the intermediate layer is formed from a thermoset material; and
a cover having a hardness of about 20 Shore D or greater, a flexural modulus of about 1,000 psi to about 30,000 psi, and a thickness of about 0.01 inches to about 0.05 inches, wherein the cover is firmed from a thermoplastic composition comprising p-phenylene diisocyanate and at least one hydroxy-terminated curing agent having the following structure;
wherein R 3 comprises at least one phthlatate group, at least one hexamethylene group, at least one bisphenol A group, or combinations thereof, and wherein n ranges from about 1 to about 25.
12. The golf ball of claim 11 , wherein the core comprises a center and an outer core layer, and wherein the center has a diameter of about 0.5 inches to about 1.3 inches.
13. The golf ball of claim 11 , wherein the thermoplastic composition further comprises at least one density-adjusting filler.
14. The golf ball of claim 11 , wherein the thermoset material comprises polyurethane, polyurea, or polybutadiene.
15. The golf ball of claim 11 , wherein the thermoplastic composition comprises an additional curing agent.
16. The golf ball of claim 15 , wherein the additional curing agent comprises hydroxy-terminated curing agents, amine-terminated curing agents, or a combination thereof.
17. The golf ball of claim 11 , wherein the layer has a first hardness and the cover has a second hardness, and wherein the ratio of the second hardness to first hardness is about 1.33 or less.
18. The golf ball of claim 17 , wherein the ratio of the second hardness to first hardness is about 1.14 or less.
19. The golf ball of claim 11 , wherein the cover has a hardness of about 54 Shore D to 72 Shore D.
20. The golf ball of claim 11 , wherein the at least one hydroxy-terminated curing agent s selected from the group consisting of poly(phthalate carbonate)glycol, poly(hexamethylene carbonate)glycol, polycarbonate polyols containing bisphenol A, and mixtures thereof.