White light emitting phosphor blends for LED devices
View Patent ↗There is provided white light illumination system including a radiation source, a first luminescent material having a peak emission wavelength of about 575 to about 620 nm, a second luminescent material having a peak emission wavelength of about 495 to about 550 nm, which is different from the first luminescent material and a third luminescent material having a peak emission wavelength of about 420 to about 480 nm, which is different from the first and second luminescent materials. The LED may be a UV LED and the luminescent materials may be a blend of three or four phosphors. The first phosphor may be an orange emitting Eu 2+ , Mn 2+ activated strontium pyrophosphate, Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ . The second phosphor may be a blue-green emitting Eu 2+ activated barium silicate, (Ba,Sr,Ca) 2 SiO 4 :Eu 2+ . The third phosphor may be a blue emitting SECA phosphor, (Sr,Ba,Ca) 5 (PO 4 ) 3 Cl:Eu 2+ . Optionally, the fourth phosphor may be a red emitting Mn 4+ activated magnesium fluorogermanate, 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ . A human observer perceives the combination of the orange, blue-green, blue and/or red phosphor emissions as white light.
1. A white light emitting phosphor blend comprising at least three phosphors, wherein the white light emitted by the phosphor blend in response to incident radiation having a peak wavelength between 360 and 420 nm comprises a color temperature between 3000K and 6500K, a CRI above 70 and an efficacy above 200 lm/W;
wherein the efficacy is above 264 lm/W and the color temperature is between 3300K and 4100K for incident radiation having a peak wavelength between 370 and 405 nm; and
wherein the phosphor blend comprises:
about 55 to about 75 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phoshor;
about 11 to about 22 weight percent of at least one of (Ba,Sr,Ca) 2 SiO 4 :Eu 2+ phosphor; and
about 13 to about 22 weight percent of at least one of (Sr,Ba,Ca,Mg) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor.
2. The phosphor blend of claim 1 , wherein the phosphor blend comprises;
about 57.5 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 21.5 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor; and
about 21 weight percent of the at least one of (Sr,Ba,Ca) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor.
3. The phosphor blend of claim 1 , wherein the phosphor blend comprises:
about 61.4 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 19.4 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor; and
about 19.2 weight percent of the at least one of (Sr,Ba,Ca) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor.
4. The phosphor blend of claim 1 , wherein the phosphor blend comprises:
about 73.7 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2 phosphor;
about 12.1 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor; and
about 14.2 weight percent of the at least one of (Sr,Ba,Ca,) 5 (PO 4 ) 3 Cl:Eu 2 + phosphor.
5. The phosphor blend of claim 1 , wherein the CRI is above 90.
6. The phosphor blend of claim 5 , further comprising a fourth phosphor comprising 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ .
7. A white light emitting phosphor blend comprising at least three phosphors, wherein the white light emitted by the phosphor blend in response to incident radiation having a peak wavelength between 360 and 420 nm comprises a color temperature between 3000K and 6500K, a CRI above 70 and an efficacy above 200 lm/W;
wherein the efficacy is above 264 lm/W and the color temperature is between 3300K and 4100K for incident radiation having a peak wavelength between 370 and 405 nm;
wherein the CRI is above 90; and
wherein the phosphor blend comprises:
about 11 to about 43 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 9 to about 15 weight percent (Ba,Sr,Ca) 2 SiO 4 :Eu 2+ phosphor;
about 6 to about 14 weight percent of at least one of(Sr,Ba,Ca,Mg) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor; and
about 30 to about 71 weight percent 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ phosphor.
8. The phosphor blend of claim 7 , wherein the efficacy is above 340 lm/W.
9. The phosphor blend of claim 7 , wherein the phosphor blend comprises:
about 12.7 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 10 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor;
about 7.4 weight percent of the at least one of (Sr,Ba,Ca,Mg) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor; and
about 69.9 weight percent 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ phosphor.
10. The phosphor blend of claim 7 , wherein the phosphor blend comprises:
about 17.6 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 11.8 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor;
about 9 weight percent of the at least one of (Sr,Ba,Ca) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor; and
about 61.6 weight percent 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ phosphor.
11. The phosphor blend of claim 7 , wherein the phosphor blend comprises:
about 41.5 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 14.2 weight percent (Ba 0.65 ,Sr 0.2 ,Ca 0.1 Eu 0.05 ) 2 SiO 4 phosphor;
about 12.8 weight percent of the at least one of (Sr,Ba,Ca) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor; and
about 31.5 weight percent 3.5MgO*0.5MgF 2 *GeO 2 :Mn 4+ phosphor.
12. A white light emitting phosphor blend comprising at least three phosphors, wherein the white light emitted by the phosphor blend in response to incident radiation having a peak wavelength between 360 and 420 nm comprises a color temperature between 3000K and 6500K, a CRI above 70 and an efficacy above 200 lm/W; and wherein the phosphor blend comprises:
about 55 to about 75 weight percent Sr 2 P 2 O 7 :Eu 2+ , Mn 2+ phosphor;
about 11 to about 22 weight percent of at least one of (Ba,Sr,Ca) 2 SiO 4 :Eu 2+ phosphor; and
about 13 to about 22 weight percent of at least one of (Sr, Ba,Ca,Mg) 5 (PO 4 ) 3 Cl:Eu 2+ phosphor.