Silica-rubber mixtures having improved hardness
View Patent ↗A method for increasing the hardness of silica/rubber mixtures includes blending with the mixture at least one silane and a hardness-increasing amount of at least one member selected from the group consisting of thixotropic fumed silica, precipitated silica and an MQ resin, wherein Q is SiO 4/2 , M is R 1 R 2 R 3 SiO 1/2 , and R 1 ,R 2 ,and R 3 are the same or different functional or non-functional organic groups, carbon black, a thermoplastic resin or a thermosetting resin.
1. A method for increasing the hardness of silica/rubber mixtures comprising blending with said mixture at least one silane and a hardness-increasing amount of at least one member selected from the group consisting of thixotropic fumed silica, precipitated silica wherein the total amount of silica is from 80 phr to 110 phr, an MQ resin wherein Q is SiO 4/2 , M is R a R b R c SiO 1/2 , and R a ,R b ,and R c are the same or different functional or non-functional organic groups, a thermoplastic resin selected from the group consisting of high-density polyethylene, ultra high molecular weight polyethylene and low density-polyethylene and a thermosetting resin, wherein the silane is 3-octanoylthio-1-propyltriethoxysilane.
2. The method of claim 1 wherein the at least one member is thixotropic-(hydrophilic and hydrophobic) fumed (pyrogenic) silica.
3. The method of claim 2 wherein the silica/rubber mixture further comprises an inorganic filler.
4. The method of claim 3 wherein the inorganic filler is selected from the group consisting of titanium dioxide, aluminosilicate, alumina, calcium carbonate, carbon fibers, glass fibers, kaolin clay, mica, talc and wollastonite.
5. The method of claim 1 wherein the member is precipitated silica.
6. The method of claim 5 wherein the silica/rubber mixture further comprises an inorganic filler.
7. The method of claim 6 wherein the inorganic filler is selected from the group consisting of titanium dioxide, aluminosilicate, alumina, calcium carbonate, carbon fibers, glass fibers, kaolin clay, mica, talc and wollastonite.
8. A method for increasing the hardness of silica/rubber mixtures comprising blending with said mixture at least one silane and a hardness-increasing amount of an MQ resin wherein Q is SiO 4/2 , M is R a R b R c SiO 1/2 , and R a , R b , and R c are the same or different functional or non-functional organic groups, wherein the silane is a blocked mercaptosilane, and wherein the silica/rubber mixture optionally includes inorganic filler,
and wherein said hardness increasing amount is sufficient to achieve a Shore A hardness of the silica/rubber mixture of from 56 to 63 and which is above the amount necessary to achieve equivalent Shore A hardness of the silica/rubber mixture as compared with the use of an equivalent molar amount of bis-(triethoxysilylpropyldisulfide) as the silane.
9. A method for increasing the hardness of silica/rubber mixtures comprising blending with said mixture at least one silane and a hardness-increasing amount of an MQ resin wherein Q is SiO 4/2 , M is R a R b R c SiO 1/2 , and R a , R b , and R c are the same or different functional or non-functional organic groups, wherein the silane is 3-octanoylthio-1-propyltriethoxysilane.
10. The method of claim 8 wherein the silica/rubber mixture further comprises an inorganic filler.
11. The method of claim 10 wherein the inorganic filler is selected from the group consisting of titanium dioxide, aluminosilicate, alumina, calcium carbonate, carbon fibers, glass fibers, kaolin clay, mica, talc and wollastonite.
12. The method of claim 1 further including the step of blending carbon black into the mixture.
13. The method of claim 1 wherein the at least one member is the thermoplastic resin.
14. The method of claim 1 wherein the at least one member is a thermosetting resin.
15. An article of manufacture comprising a silica/rubber mixture hardened by blending with said mixture at least one silane and a hardness-increasing amount of at least one member selected from the group consisting of thixotropic fumed silica, precipitated silica wherein the total amount of silica is from 80 phr to 110 phr, an MQ resin wherein Q is SiO 4/2 , M is R a R b R c SiO 1/2 and R a , R b , and R c are the same or different functional or non-functional organic groups, a thermoplastic resin selected from the group consisting of high-density polyethylene, ultra high molecular weight polyethylene, low density-polyethylene and a thermosetting resin, wherein the silane is 3-octanoylthio-1-propyltriethoxysilane.
16. An article of manufacture comprising a silica/rubber mixture hardened by blending with said mixture at least one silane and a hardness-increasing amount of an MQ resin wherein Q is SiO 4/2 , M is R a R b R c SiO 1/2 , and R a , R b , and R c are the same or different functional or non-functional organic groups, wherein the silane is 3-octanoylthio-1-propyltriethoxysilane, and wherein the silica/rubber mixture optionally includes inorganic filler, and wherein said hardness increasing amount is sufficient to achieve a Shore A hardness of the silica/rubber mixture of from 56 to 63 and which is above the amount necessary to achieve equivalent Shore A hardness of the silica/rubber mixture as compared with the use of an equivalent molar amount of bis-(triethoxysilylpropyldisulfide) as the silane.
17. The article of claim 16 wherein said article is a tread portion of a tire.
18. A method for increasing the hardness of silica/rubber mixtures comprising blending with said mixture at least one silane coupling agent and a hardness-increasing amount of silica wherein the total amount of silica is from 80 phr to 110 phr, wherein the silane coupling agent is 3-octanoylthio-1-propyltriethoxysilane,
and wherein said hardness increasing amount is sufficient to achieve a Shore A hardness of from 56 to 63 and which is above the amount necessary to achieve equivalent Shore A hardness of the silica/rubber mixture as compared with the use of an equivalent molar amount of bi s-(triethoxysilylpropyldisulfide) as the silane.
19. An article of manufacture comprising a silica/rubber mixture hardened by blending with said mixture at least one silane coupling agent and a hardness-increasing amount of silica wherein the total amount of silica is from 80 phr to 110 phr, wherein the silane coupling agent is 3-octanoylthio-1-propyltriethoxysilane, and wherein the silica/rubber mixture optionally includes inorganic filler,
and wherein said hardness increasing amount is sufficient to achieve a Shore A hardness of from 56 to 63 and which is above the amount necessary to achieve equivalent Shore A hardness of the silica/rubber mixture as compared with the use of an equivalent molar amount of bis-(triethoxysilylpropyldisulfide) as the silane.
20. The method of claim 8 wherein the silica/rubber mixture comprises a rubber selected from the group consisting of solution styrene-butadiene rubber (SSBR), styrene-butadiene rubber (SBR), natural rubber (NR), polybutadiene (BR), ethylene-propylene co- and terpolymers (EP, EPDM), and acrylonitrile-butadiene rubber (NBR), isoprene rubber, 1 ,3-butadiene, styrene and methyl styrene, natural or synthetic cis-1 ,4-polyisoprene rubber, emulsion polymerization prepared styrene/butadiene copolymer rubber, organic solution polymerization prepared styrene/butadiene rubber, 3,4-polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubber, cis-1 ,4-polybutadiene, vinyl polybutadiene rubber styrene/isoprene copolymers, emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber.