Corrosion resistant films based on ethylenically unsaturated monomer modified epoxy emulsions
View Patent ↗The invention provides high solids epoxy-based autodeposition coating materials and a means to obtain the high solids epoxy-based autodeposition coating materials that eliminates/minimizes the need for process solvents. An epoxy pre-polymer is used. The epoxy pre-polymer is combined with ethylenically unsaturated monomer, as an alternative to organic solvent, to yield an epoxy-monomer blend, which may be blended with other coating components and additives. The resulting blend is then dispersed in water with surfactant and the ethylenically unsaturated monomer is polymerized (in the presence of other formulation components) to yield a dispersion. The dispersion may then be used as one component of a coating formulation. The coating formulation can then be applied to materials and cured to form a final coating.
1. A process for making an autodepositing epoxy-based dispersion, the process comprising the steps of:
(a) dissolving and/or reducing an epoxy pre-polymer with at least one ethylenically unsaturated monomer to form a mixture wherein the at least one ethylenically unsaturated monomer is an anionic functional monomer;
(b) dispersing the mixture of step (a) in water with at least one surfactant to form a fine particle dispersion; and
(c) polymerizing the at least one ethylenically unsaturated monomer contained in the fine particle dispersion to form an epoxy dispersion,
wherein at least one water soluble initiator and/or at least one organic soluble initiator is added prior to step (c) and wherein at least one latent curing agent is incorporated into the mixture before the at least one ethylenically unsaturated monomer is polymerized.
2. The process of claim 1 , wherein step (b) comprises the steps of:
dispersing the mixture of step (a) in water with the at least one surfactant to form a crude dispersion; and
mechanically dispersing the crude dispersion to form a fine particle dispersion.
3. The process of claim 1 , wherein at least one water-soluble initiator is added after step (a) and prior to step(c) and/or at least one organic soluble initiator is added before step (b).
4. The process of claim 1 , wherein step (c) is carried out by heating the fine particle dispersion.
5. The process of claim 1 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
6. The process of claim 1 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.
7. The process of claim 1 , wherein at least one further component is added prior to step (c), wherein the at least one further component is selected from the group consisting of curing agents, coalescing solvents, level agents, and mixtures thereof.
8. The process of claim 1 , wherein the anionic functional monomer is select from the group consisting of 2-sulfoethyl methacrylate, 2-acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, and vinylphosphonic acid.
9. The process of claim 1 , wherein the anionic functional monomer is a phosphate ester monomer.
10. An stable autodepositing epoxy dispersion produced according to the process of claim 1 .
11. An autodepositing coating composition comprising:
(a) at least one epoxy dispersion produced by the process of claim 1 ;
(b) water; and
(c) at least one autodeposition accelerator.
12. A process for making an autodepositing epoxy-based dispersion, the process comprising the steps of:
(a) dissolving and/or reducing an epoxy pre-polymer with at least one ethylenically unsaturated monomer to form a mixture;
(b) dispersing the mixture of step (a) in water with at least one surfactant to form a fine particle dispersion; and
(c) polymerizing the at least one ethylenically unsaturated monomer contained in the fine particle dispersion to form an epoxy dispersion,
wherein at least one water soluble initiator and/or at least one organic soluble initiator is added prior to step (c) and at least one phosphate ester monomer is added after step (b) and prior to or during step (c).
13. The process of claim 12 , wherein step (b) comprises the steps of:
dispersing the mixture of step (a) in water with the at least one surfactant to form a crude dispersion; and
mechanically dispersing the crude dispersion to form a fine particle dispersion.
14. The process of claim 12 , wherein at least one water-soluble initiator is added after step (a) and prior to step (c) and/or at least one organic soluble initiator is added before step (b).
15. The process of claim 12 , wherein step (c) is carried out by heating the fine particle dispersion.
16. The process of claim 12 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
17. The process of claim 12 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.
18. The process of claim 12 , wherein at least one further component is added prior to step (c), wherein the at least one further component is selected from the group consisting of curing agents, coalescing solvents, level agents, and mixtures thereof.
19. A stable autodepositing epoxy dispersion comprising
(a) an epoxy pre-polymer;
(b) at least one ethylenically unsaturated monomer polymerized through a heterophase polymerization process; and
(c) at least one latent curing agent,
wherein the epoxy dispersion further comprises dispersion particles and components (a), (b), and (c) are all present in one or more of the dispersion particles and the at least one ethylenically unsaturated monomer is an anionic functional monomer.
20. The stable autodepositing epoxy dispersion of claim 19 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
21. The stable autodepositing epoxy dispersion of claim 19 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.
22. The stable autodepositing epoxy dispersion of claim 19 , further comprising at least one further component selected from the group consisting of colorants, pigments, coalescing solvents, level agents, and mixtures thereof.
23. The stable autodepositing epoxy dispersion of claim 19 , wherein the anionic functional monomer is select from the group consisting of 2-sulfoethyl methacrylate, 2-acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, and vinylphosphonic acid.
24. The stable autodepositing epoxy dispersion of claim 19 , wherein the anionic functional monomer is a phosphate ester monomer.
25. A stable autodepositing epoxy dispersion comprising
(a) an epoxy pre-polymer; and
(b) at least one ethylenically unsaturated monomer polymerized through a heterophase polymerization process, wherein at least one ethylenically unsaturated monomer is a phosphate ester monomer,
and further wherein the epoxy dispersion further comprises dispersion particles and components (a) and (b) are both present in one or more of the dispersion particles.
26. The autodepositing epoxy dispersion of claim 25 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
27. The autodepositing epoxy dispersion of claim 25 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.
28. The autodepositing epoxy dispersion of claim 25 , further comprising at least one further component selected from the group consisting of curing agents, colorants, pigments, coalescing solvents, level agents, and mixtures thereof.
29. The autodepositing epoxy dispersion of claim 25 , further comprising at least one latent curing agent, wherein components (a), (b), and the at least one latent curing agent are all present in one or more of the dispersion particles.
30. An autodepositing coating composition comprising:
(a) at least one epoxy dispersion comprising: (i) an epoxy pre-polymer; (ii) at least one ethylenically unsaturated monomer polymerized through a heterophase polymerization process; and (iii) at least one latent curing agent, wherein the epoxy dispersion further comprises dispersion particles and components (i), (ii), and (iii) are all present in one or more of the dispersion particles;
(b) water; and
(c) at least one autodeposition accelerator.
31. The autodepositing coating composition of claim 30 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
32. The autodepositing coating composition of claim 30 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.
33. The autodepositing coating composition of claim 30 , further comprising at least one further component selected from the group consisting of colorants, pigments, coalescing solvents, level agents, and mixtures thereof.
34. The autodepositing coating composition of claim 30 , wherein the at least one ethylenically unsaturated monomer is selected from the group consisting of acrylic acid, methacrylic acid, esters of acrylic acid, esters of methacrylic acid, acrylonitrile, methacrylonitrile, acrylamide , methacrylamide, and styrene.
35. The autodepositing coating composition of claim 30 , wherein the at least one ethylenically unsaturated monomer is an anionic functional monomer.
36. An autodepositing coating composition comprising:
(a) at least one epoxy dispersion comprising (i) an epoxy pre-polymer and (ii) at least one ethylenically unsaturated monomer polymerized through a heterophase polymerization process, wherein the epoxy dispersion further comprises dispersion particles and components (i) and (ii) are both present in one or more of the dispersion particles;
(b) water; and
(c) at least one autodeposition accelerator.
37. The autodepositing epoxy-acrylic coating composition of claim 36 , wherein at least one of the ethylenically unsaturated monomers is a phosphate ester monomer.
38. The autodepositing coating composition of claim 37 , wherein the epoxy pre-polymer is derived from epoxy resin prepared by reacting a diglycidyl ether of a polyhydric phenol.
39. The autodepositing coating composition of claim 37 , wherein the epoxy pre-polymer is derived from one or more epoxy resins conforming to the general chemical structure:
wherein A is
and n is 0 or an integer from 1 to 50.