Infrared absorbing blue glass composition
View Patent ↗A blue glass composition comprises a soda-lime-silica base and a colorant portion consisting essentially of about 0.4 to 0.65 weight percent total iron oxide, about 0.1 to 0.3 weight percent manganese oxide, and cobalt oxide in an amount effective to produce a cobalt concentration of about 0.0002 to 0.0013 weight percent (about 2 to 13 ppm). The glass is characterized by a ratio of ferrous oxide to total iron oxide between about 0.43 and 0.58. The glass composition exhibits a combination of high visible transmittance, high infrared absorption and enhanced blue coloration. This is attributed in large part to the combination of ferrous oxide and cobalt oxide and to the effect of manganese oxide in reducing iron sulfide formation and thereby avoiding amber coloration.
1. A blue glass composition for automotive glazing comprising a soda-lime-silica base and a colorant portion, said colorant portion, consisting essentially of:
0.4 to 0.65 weight percent total iron oxide in the form of Fe 2 O 3 ,
greater than about 0.1 to about 0.3 weight percent manganese oxide,
cobalt oxide in an amount to produce a cobalt concentration of about 0.0002 to 0.0013 weight percent,
wherein the redox ratio is between about 0.43 and 0.58,
said blue glass composition being characterized by between about 68 to 76 percent illuminant A transmittance, about 54 to 64 percent ultraviolet transmittance, about 12 to 22 percent infrared transmittance, a dominant wavelength between about 486 and 490 nanometers, and a purity excitation between about 7 and 11 percent, as determined at 4.0 mm thickness.
2. The blue glass composition of claim 1 wherein the base comprises:
about 68 to 75 weight percent SiO 2 ,
about 10 to 18 weight percent Na 2 O,
about 5 to 15 weight percent CaO,
0 to about 10 weight percent MgO,
0 to about 5 weight percent Al 2 O 3 ; and
0 to about 5 weight percent K 2 O.
3. The blue glass composition of claim 1 wherein the base is characterized by a total of Na 2 O and K 2 O between about 10 and 20 weight percent.
4. The blue glass composition of claim 1 wherein the dominant wavelength is between about 488 and 489 nanometers.
5. The blue glass composition of claim 1 wherein the total amount of iron oxide is between about 0.45 and 0.55 weight percent.
6. The blue glass composition of claim 1 wherein the manganese oxide is between about 0.14 and 0.2 weight percent.
7. The blue glass composition of claim 1 wherein the cobalt concentration due to cobalt oxide is between about 0.0003 and 0.0010 weight percent.
8. A blue glass composition for automotive or architectural glazing comprising a soda-lime-silica base and a colorant portion, said colorant portion consisting essentially of:
0.4 to 0.65 weight percent total iron oxide in the form of Fe 2 O 3 ,
greater than about 0.1 to about 0.3 weight percent manganese oxide,
cobalt oxide in an amount to produce a cobalt concentrat on of about 0.0002 to 0.0013 weight percent,
wherein the redox ratio is between about 0.43 and 0.58,
said blue glass composition being characterized by between about 68 to 76 percent illuminant A transmittance, about 54 to 64 percent ultraviolet transmittance, about 12 to 22 percent infrared transmittance, a dominant wavelength between about 486 and 490 nanometers, and a purity excitation between about 7 and 11 percent, as determined at 4.0 mm thickness.
9. The blue glass composition of claim 1 wherein the blue glass contains between about 0.03 and 0.12 weight percent SO 3 .
10. The blue glass composition of claim 1 wherein the blue glass contains between about 0.05 and 0.08 weight percent SO 3 .