High melt integrity battery separator for lithium ion batteries
View Patent ↗The battery separator for a lithium battery is made from a nonwoven flat sheet material having high temperature melt integrity, a microporous membrane having low temperature shutdown properties, and an adhesive bonding the nonwoven flat sheet to the microporous membrane and being adapted for swelling when contacted by an electrolyte.
1. A battery separator comprising:
a nonwoven flat sheet having a high temperature melt integrity;
a microporous membrane having low temperature shutdown properties; and
an adhesive bonding said nonwoven flat sheet to said microporous membrane, said adhesive being a swellable polymer selected from the group consisting of polyvinylidene fluoride; polyurethane; polyethylene oxide; polyacrylonitrile; polyacrylamide; polyvinyl acetate; polyvinylpyrrolidone; polytetraethylene glycol diacrylate; copolymers of any the foregoing and combinations thereof.
2. The battery separator of claim 1 wherein membrane being made from a thermoplastic polymer.
3. The battery separator of claim 1 wherein said nonwoven flat sheet being made of polymers selected from the group consisting of thermoplastic polymers, cellulosic, and/or ceramics.
4. A battery made with separator of claim 1 .
5. A battery separator comprising:
a nonwoven flat sheet having a high temperature melt integrity;
a microporous membrane having low temperature shutdown properties; and
an adhesive bonding said nonwoven flat sheet to said microporous membrane, said adhesive comprises a swellable polymer and a wetting agent.
6. The battery separator of claim 5 wherein said swellable polymer being selected from the group consisting of polyvinylidene fluoride; polyurethane; polyethylene oxide; polyacrylonitrile; polymethylacrylate; poly(methylmethacrylate); polyacrylamide; polyvinyl acetate; polyvinylpyrrolidone; polytetraethylene glycol diacrylate; copolymers of any the foregoing and combinations thereof.
7. The battery separator of claim 5 wherein said wetting agent being selected from the group consisting of phthalate-based esters, cyclic carbonates, polymeric carbonates, and mixtures thereof.
8. The battery separator of claim 5 wherein said membrane being made from a thermoplastic polymer.
9. The battery separator of claim 8 wherein said thermoplastic polymer being selected from the group consisting of polystyrenes, polyvinyl chlorides, polyacrylics, polyacetals, polyamides, polycarbonates, polyesters, polyetherimides, polyimides, polyketones, polyphenylene ethers, polyphenylene sulfides, and polysulfones.
10. The battery separator of claim 5 wherein said nonwoven flat sheet being made of polymers selected from the group consisting of thermoplastic polymers, cellulosic, and/or ceramics.
11. A battery separator comprising:
a nonwoven flat sheet having a high temperature melt integrity, said nonwoven flat sheet further comprising a coating or surface treatment;
a microporous membrane having low temperature shutdown properties; and
an adhesive bonding said nonwoven flat sheet to said microporous membrane.
12. The battery separator of claim 11 wherein said coating or surface treatment being a ceramic material.
13. The battery separator of claim 12 wherein said ceramic material being selected from the group of alumina, silica, and zirconia compounds and combinations thereof.
14. The battery separator of claim 11 wherein said nonwoven flat sheet being made of polymers selected from the group consisting of thermoplastic polymers, cellulosic, and/or ceramics.
15. The battery separator of claim 11 wherein said membrane being made from a thermoplastic polymer.
16. The battery separator of claim 11 wherein said thermoplastic polymer being selected from the group consisting of polystyrenes, polyvinyl chlorides, polyacrylics, polyacetals, polyamides, polycarbonates, polyesters, polyetherimides, polyimides, polyketones, polyphenylene ethers, polyphenylene sulfides, and polysulfones.
17. Method of making separator comprising the steps of
providing a nonwoven flat sheet,
providing a microporous membrane,
providing an adhesive solution comprising a solvent, a swellable polymer, and a wetting agent,
coating said sheet or said membrane or both said sheet and membrane with the adhesive solution,
laminating together the nonwoven flat sheet and the membrane, and
forming thereby the separator.
18. The method of claim 17 wherein laminating further comprises applying temperature of about 120–135° C.
19. The method of claim 17 further comprising washing the laminated separator with a solvent.