Curable compositions
View Patent ↗The present invention has for its object to provide a curable composition which, despite its low viscosity, gives a cured product with a high gel fraction, low residual tack, low modulus, high elongation, and good flexibility. The present invention relates to a curable composition comprising the following two components: (A) a vinyl polymer having at least one crosslinking silyl group on the average per molecule: and (B) a photocurable substance, (C) an air oxidation-curable substance, (D) a high molecular plasticizer, (E) a reactive plasticizer or (F) a compound having one silanol group in its molecule and/or a compound capable of reacting with moisture to give a compound having one silanol group in the molecule.
1. A curable composition comprising the following two components:
(A3) a vinyl polymer having at least one crosslinking functional group on the average per molecule and
(D) a high molecular plasticizer having a number average molecular weight of 500 or over.
2. The curable composition according to claim 1
wherein the vinyl polymer (A3) is a molecular weight distribution value of less than 1.8.
3. The curable composition according to claim 1 wherein the vinyl polymer (A3) is a (meth)acrylic polymer.
4. The curable composition according to claim 1 wherein the vinyl polymer (A3) is an acrylic polymer.
5. The curable composition of any of claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) is a crosslinking silyl group.
6. The curable composition according to claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) is an alkenyl group.
7. The curable composition according to claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) is a hydroxyl group.
8. The curable composition according to claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) is an amino group.
9. The curable composition according to claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) has a polymerizable carbon-carbon double bond.
10. The curable composition according to claim 1
wherein the crosslinking functional group of the vinyl polymer (A3) is an epoxy group.
11. The curable composition according to claim 1
wherein the vinyl polymer (A3) has a main chain produced by living radical polymerization technique.
12. The curable composition according to claim 11
wherein the vinyl polymer (A3) has a main chain produced by atom transfer radical polymerization technique.
13. The curable composition according to claim 12
wherein the atom transfer radical polymerization technique is carried out by using, as the catalyst, a transition metal complex whose center metal belongs to group 7, 8, 9, 10 or 11 of the periodic table of the elements.
14. The curable composition according to claim 13
wherein the transition metal complex is a complex of copper, nickel, ruthenium or iron.
15. The curable composition according to claim 14
wherein the transition metal complex is a complex of copper.
16. The curable composition according to claim 1
wherein the high molecular plasticizer (D) has a number average molecular weight of 500 to 15000.
17. The curable composition according to claim 16
wherein the high molecular plasticizer (D) has a number average molecular weight of 800 to 10000.
18. The curable composition according to claim 17
wherein the high molecular plasticier (D) has a number average molecular weight of 1000 to 8000.
19. The curable composition according to claim 1 wherein the high molecular plasticizer (D) is a vinyl polymer.
20. The curable composition according to claim 19
wherein the high molecular plasticizer (D) has a molecular weight distribution value of less than 1.8.
21. The curable composition according to claim 19 wherein the high molecular plasticizer (D) is a (meth)acrylic polymer.
22. The curable composition according to claim 20 wherein the high molecular plasticizer (D) is an acrylic polymer.
23. The curable composition according to claim 20
wherein the high molecular plasticizer (D) is produced by living radical polymerization technique.
24. The curable composition according to claim 23
wherein the high molecular plasticizer (D) is produced by atom transfer radical polymerization technique.
25. The curable composition according to claim 1
wherein the addition amount of the high molecular plasticizer (D) is 5 to 150 weight parts based on 100 weight parts of the vinyl polymer (A3) having at least one crosslinking functional group.