Detoxification of solid freeform fabrication materials
View Patent ↗A detoxification process for rendering three-dimensional objects formed by solid freeform fabrication techniques biocompatible for use in long-term dermal contact applications. The process nullifies cytotoxins normally present in objects formed by solid freeform fabrication techniques rendering such techniques as viable for the production of biocompatible devices such as stents, artery valve components, bone implant supports, pacemaker shells, surgical tools, and the like. In one embodiment, a custom hearing aid shell is produced by stereolithography from an acrylate photopolymer resin that was detoxified for long-term dermal contact application. The detoxification process makes three-dimensional objects created by solid freeform fabrication techniques available for products requiring biocompatibility.
1. A hearing aid shell produced according to a method of forming and detoxifying a three-dimensional object formed by solid freeform fabrication, the hearing aid shell being detoxified for at least long-term dermal contact biocompatibility, the method comprising:
forming in a layerwise fashion a preliminary object in successive layers with a build material the preliminary object containing cytotoxins;
nullifying the cytotoxins in the preliminary object by subjecting the preliminary object to vapor treatment to establish a biocompatible three-dimensional hearing aid shell.
2. The hearing aid shell of claim 1 wherein the step of nullifying the cytotoxins is accomplished individually or in any combination of the following steps:
entrapping at least some of the cytotoxins within the three-dimensional object by advancing a state of cure of the preliminary object;
decomposing at least some of the cytotoxins into a non-toxic state within the three-dimensional object by subjecting the preliminary object to thermal energy; or
transforming at least some of the cytotoxins into a non-toxic state within the three-dimensional object by advancing the state of cure of the object.
3. The hearing aid shell of claim 1 wherein the build material is photocurable and is applied in successive layers in the form of paste, liquid, or gel.
4. The hearing aid shell of claim 3 wherein the build material is a photocurable material selected from the group consisting of an acrylate, an epoxy, or an epoxy/acrylate blend.
5. The hearing aid shell of claim 1 wherein the vapor treatment is applied for at least about 5 minutes.
6. The hearing aid shell of claim 5 wherein the vapor treatment is performed with steam.
7. The hearing aid shell of claim 6 wherein the temperature of the steam is between about 121° C. and about 124° C. and is applied for about 30 minutes.
8. The hearing aid shell of claim 1 wherein the hearing aid shell is UV postcured prior to subjecting to vapor treatment.
9. A bearing aid shell produced according to a method of forming and detoxifying a three-dimensional object fanned by solid freeform fabrication, the hearing aid shell being detoxified for at least long-term dermal contact biocompatibility, the method comprising:
forming in a layerwise fashion a preliminary object in successive layers with a build material, the preliminary object containing cytotoxins;
subjecting the preliminary object to vapor treatment in a medium for a sufficient period of time so as to nullify the cytotoxins in the preliminary object and thereby establish a biocompatible three-dimensional object.
10. The hearing aid shell of claim 9 wherein the medium is water or a solvent.
11. The hearing aid shell of claim 10 wherein the vapor treatment is applied for at least about 5 minutes.
12. The hearing aid shell of claim 11 wherein the medium is steam.
13. The hearing aid shell of claim 12 wherein the temperature of the steam is between about 121° C. and about 124° C. for about 30 minutes.
14. The hearing aid shell of claim 9 wherein the hearing aid shell is UV postcured prior to subjecting to vapor treatment.