View Patent ↗A dielectric composition that can be fired at a temperature of below 900° C. The dielectric composition has a dielectric constant of 25–35 and a quality factor (Qxf) of 6,000–20,000 GHz. The composition comprises 3–16 wt % of K 2 O—Na 2 O—Li 2 O—B 2 O 3 —SiO 2 system glass frit and 84–97 wt % of BaO—TiO 2 system dielectric ceramics. The composition can be effectively applied to construct a part of a ceramic multi-layer packaging as a resonator form such as a filter or an antenna, etc.
1. A dielectric composition comprising:
84–97 wt % of BaO-nTiO 2 ; and
3–16 wt % of glass frit consisting of Li 2 O, B 2 O 3 , SiO 2 , Na 2 O and K 2 O
wherein said n=4.0–4.5 and said dielectric composition has a firing temperature of 875° C.–950° C. and a quality factor (Q*f) of 6,000–20,000.
2. The composition of claim 1 , wherein a wt % of the SiO 2 is 7–40, a wt % of the B 2 O 3 is 33–60, and a wt % of the Li 2 O is 18–41.
3. The composition of claim 2 , wherein the glass frit has a dielectric constant of 6.4–8.5, a glass transition temperature of 350–510° C. and a dielectric loss value of 0.3–1.0%.