Alkaline cell with performance enhancing additives
View Patent ↗Alkaline electrochemical cells having extended service life and acceptable gassing and corrosion properties are disclosed. An amphoteric surfactant can be incorporated into the gelled anode mixture of an alkaline electrochemical cell, optionally with an organic phosphate ester surfactant or a sulfonic acid type organic surfactant or both. Zinc particles having a defined distribution of particle sizes can also be incorporated into a zinc anode. The electrolyte included in the anode mixture can have a reduced hydroxide concentration.
1. A gelled anode mixture comprising a metal alloy powder, a gelling agent, an alkaline electrolyte having a hydroxide concentration less than 40 weight %, and at least one amphoteric surfactant.
2. A gelled anode mixture as claimed in claim 1 wherein the amphoteric surfactant has a formula
wherein: R1 is an alkyl group having between 8 and 30 unbranched carbon atoms; R2 is an alkyl group having between 1 to about 6 unbranched carbon atoms, optionally substituted with 1 or more hydroxyl substituents; R3 is selected from a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 to 10 propylene oxide units; and, X is an anionic acid group, an anionic acid ester, or an alkali metal salt of an anionic acid or acid ester.
3. A gelled anode mixture as claimed in claim 2 further comprising an amphoteric surfactant having a formula
wherein: R4 is an unbranched alkyl group having between 8 and 30 unbranched carbon atoms that form an aliphatic fatty amine when bound to the nitrogen atom; R5 is selected from a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 and 10 propylene oxide units; and, R6 is selected from hydrogen, a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 and 10 propylene oxide units.
4. A gelled anode mixture as claimed in claim 1 further comprising a surfactant having a general formula Y SOx − or a salt thereof, wherein x is 3 or 4, and wherein Y is selected from the group consisting of an alkyl group, an aryl group, an alkylaryl group, and a carboxy acid group.
5. A gelled anode mixture as claimed in claim 4 wherein the Y SOx − surfactant is a salt of a sulfated octadecanoic acid.
6. A gelled anode mixture as claimed in claim 4 wherein the Y SOx − surfactant is a sodium salt of sulfated oleic acid.
7. A gelled anode mixture as claimed in claim 1 further comprising an organic phosphate ester surfactant.
8. A gelled anode mixture as claimed in claim 7 wherein the organic phosphate ester surfactant is an ethylene oxide-adduct type organic phosphate ester.
9. A gelled anode mixture as claimed in claim 7 further comprising a surfactant having a general formula Y SOx − or a salt thereof, wherein x is 3 or 4, and wherein Y is selected from the group consisting of an alkyl group, an aryl group, an alkylaryl group, and a carboxy acid group.
10. A gelled anode mixture as claimed in claim 1 , wherein the electrolyte comprises KOH.
11. An alkaline electrochemical cell comprising:
a positive current collector;
a cathode in contact with the positive current collector;
a gelled anode comprising a metal alloy powder, a gelling agent, an alkaline electrolyte having a hydroxide concentration less than 40 weight %, and at least one amphoteric surfactant;
a separator between the cathode and the anode; and
a negative current collector in electrical contact with the anode.
12. A alkaline electrochemical cell as claimed in claim 11 wherein the amphoteric surfactant has a formula
wherein: R1 is an alkyl group having between 8 and 30 unbranched carbon atoms; R2 is an alkyl group having between 1 to about 6 unbranched carbon atoms, optionally substituted with 1 or more hydroxyl substituents; R3 is selected from a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 to 10 propylene oxide units; and, X is an anionic acid group, an anionic acid ester, or an alkali metal salt of an anionic acid or acid ester.
13. A alkaline electrochemical cell as claimed in claim 12 further comprising an amphoteric surfactant having a formula
wherein: R4 is an unbranched alkyl group having between 8 and 30 unbranched carbon atoms that form an aliphatic fatty amine when bound to the nitrogen atom; R5 is selected from a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 and 10 propylene oxide units; and, R6 is selected from hydrogen, a polyethylene oxide group having between 3 and 40 ethylene oxide units and a polypropylene oxide group having between 1 and 10 propylene oxide units.
14. A alkaline electrochemical cell as claimed in claim 11 further comprising a surfactant having a general formula Y SOx − or a salt thereof, wherein x is 3 or 4, and wherein Y is selected from the group consisting of an alkyl group, an aryl group, an alkylaryl group, and a carboxy acid group.
15. A alkaline electrochemical cell as claimed in claim 14 wherein the Y SOx − surfactant is a salt of a sulfated octadecanoic acid.
16. A alkaline electrochemical cell as claimed in claim 14 wherein the Y SOx − surfactant is a sodium salt of sulfated oleic acid.
17. A alkaline electrochemical cell as claimed in claim 11 further comprising an organic phosphate ester surfactant.
18. A alkaline electrochemical cell as claimed in claim 17 wherein the organic phosphate ester surfactant is an ethylene oxide-adduct type organic phosphate ester.
19. A alkaline electrochemical cell as claimed in claim 17 further comprising a surfactant having a general formula Y SOx − or a salt thereof, wherein x is 3 or 4, and wherein Y is selected from the group consisting of an alkyl group, an aryl group, an alkylaryl group, and a carboxy acid group.
20. A gelled anode mixture comprising a metal alloy powder, a gelling agent, an alkaline electrolyte having a hydroxide concentration less than 40 weight %, and at least one amphoteric surfactant, wherein the metal alloy powder comprises zinc particles, at least 70 weight % of the particles having a particle size within a 100 micron size range distribution, the distribution having a mode between about 100 and about 300 microns.
21. A gelled anode mixture as claimed in claim 20 wherein the mode of the particle size distribution is about 100 microns.
22. A gelled anode mixture as claimed in claim 20 wherein the mode of the particle size distribution is about 150 microns.
23. A gelled anode mixture as claimed in claim 20 wherein the mode of the particle size distribution is about 250 microns.
24. A gelled anode mixture as claimed in claim 20 , wherein the electrolyte has an hydroxide concentration no higher than about 34 weight %.
25. A gelled anode mixture as claimed in claim 20 , wherein the electrolyte has an hydroxide concentration no higher than about 30 weight %.
26. A gelled anode mixture as claimed in claim 20 , wherein the electrolyte has an hydroxide concentration no higher than about 28 weight %.
27. A alkaline electrochemical cell comprising:
a positive current collector;
a cathode in contact with the positive current collector;
a gelled anode comprising a metal alloy powder, a gelling agent, an alkaline electrolyte having a hydroxide concentration less than 40 weight %, and at least one amphoteric surfactant, wherein the metal alloy powder comprises zinc particles, at least 70 weight % of the particles having a particle size within a 100 micron size range distribution, the distribution having a mode between about 100 and about 300 microns;
a separator between the cathode and the anode; and
a negative current collector in electrical contact with the anode.
28. A alkaline electrochemical cell as claimed in claim 27 wherein the mode of the particle size distribution is about 100 microns.
29. A alkaline electrochemical cell as claimed in claim 27 wherein the mode of the particle size distribution is about 200 microns.
30. A alkaline electrochemical cell as claimed in claim 27 wherein the mode of the particle size distribution is about 300 microns.
31. A alkaline electrochemical cell as claimed in claim 27 , wherein the electrolyte has an hydroxide concentration no higher than about 34 weight %.
32. A alkaline electrochemical cell as claimed in claim 27 , wherein the electrolyte has an hydroxide concentration no higher than about 30 weight %.
33. A alkaline electrochemical cell as claimed in claim 27 , wherein the electrolyte has an hydroxide concentration no higher than about 28 weight %.
34. A alkaline electrochemical cell as claimed in claim 27 , wherein the electrolyte comprises KOH.