Ink formulations and uses thereof
View Patent ↗The present invention provides a chemical ink for pad printing a medical device comprising water; a colorant; and a crosslinkable, water-soluble poly(vinyl alcohol). The ink has a viscosity of greater than 50 centipoise, and good adhesion to the medical device. Method for printing contact lenses with such ink are also disclosed.
1. An ink for pad printing a medical device comprising: from about 1% and 59% by weight of water; from about 0.5% to about 8% by weight of a colorant; and from about 1% to about 75% by weight of a binder polymer, wherein the binder polymer is a crosslinkable, water-soluble poly(vinyl alcohol) having olefinically unsaturated radicals, provided that the ink does not include a crosslinker to crosslink two or more monomers or polymer molecules, wherein the ink has a viscosity of greater than 100 centipoise, wherein the ink without crosslinker has good adhesion to a medical device, wherein the water-soluble poly(vinyl alcohol) is a crosslinkable polymer based on a polyhydroxyl compound which is a derivative of a poly(vinyl alcohol) having a molecular weight of at least about 2000 which comprises from about 0.5 to about 80%, based on the number of hydroxyl groups in the poly(vinyl alcohol), of units of the formula I, I and II, I and III, or I and II and III
in which R is alkylene having up to 12 carbon atoms, R 1 is hydrogen or lower alkyl, R 2 is an olefinically unsaturated, electron-withdrawing, crosslinkable radical, preferably having up to 25 carbon atoms, and R 3 is hydrogen, a C 1 -C 6 alkyl group or a cycloalkyl group,
wherein R and R 3 are as defined for formula I above, and R 7 is a primary, secondary or tertiary amino group or a quaternary amino group of the formula N + (R′) 3 X − , in which each R′, independently of the others, is hydrogen or a C 1 -C 4 alkyl radical and X is a counter ion,
in which R and R 3 are as defined for formula I above, and R 8 is the radical of a monobasic, dibasic or tribasic, saturated or unsaturated, aliphatic or aromatic organic acid or sulfonic acid.
2. An ink of claim 1 , wherein a color image printed on a medical device with said ink, passes an autoclave-surviving test.
3. An ink of claim 1 , wherein the viscosity is from 100 to about 1000 cps.
4. An ink of claim 3 , wherein the viscosity is between 250 and 350 cps.
5. An ink of claim 1 , wherein the colorant is selected from the group consisting of a pigment and a dye which is either sparingly soluble or insoluble in water.
6. An ink of claim 5 , comprising water in an amount of from about 26% and 30% by weight.
7. An ink of claim 5 , comprising water-soluble poly (vinyl alcohol) in an amount of from about 47% o about 71% by weight.
8. An ink of claim 5 , comprising colorant in an amount of from about 1% to 5% by weight.
9. An ink of claim 5 , wherein said colorant comprises a pigment selected from the group consisting of phthalocyanine blue, cobalt blue, phthalocyanine green, chromium sesquioxide; iron oxide pigments, and carbazole violet.
10. An ink of claim 9 , wherein said colorant comprises phthalocyanine blue.
11. An ink of claim 10 , comprising water in an amount of from about 27% and 29% by weight by weight; crosslinkable water-soluble poly (vinyl alcohol) in an amount of from about 70% to about 72% by weight; and phthalocyanine blue in an amount from about 0.5 to about 1.5% by weight.
12. An ink of claim 10 , comprising water in an amount of from about 36% to 37% by weight by weight; crosslinkable water-soluble poly (vinyl alcohol) in an amount of from about 58% to about 60% by weight; and phthalocyanine blue in an amount from about 4% to about 5% by weight.
13. An ink of claim 1 , wherein the medical device is an ophthalmic lens.
14. An ink of claim 13 , wherein the ophthalmic lens is a contact lens.
15. An ink of claim 1 , wherein said poly (vinyl alcohol) comprises multiple crosslinkable groups; and the multiple crosslinkable groups are capable of forming inter- and intra crosslinkages with other crosslinkable groups of the same type or different type so that a macromolecular matrix can be formed to bind or trap pigments when cured.
16. An ink of claim 1 , wherein R 2 is a radical of the formula V
—[CO—NH—(R 5 —NH—CO—O) q —R 6 —O] p —CO—R 4 (V)
in which p and q, independently of one another, are zero or one, and R 5 and R 6 , independently of one another, are lower alkylene having 2 to 8 carbon atoms, arylene having 6 to 12 carbon atoms, a saturated bivalent cycloaliphatic group having 6 to 10 carbon atoms, arylenealkylene or alkylenearylene having 7 to 14 carbon atoms or arylenealkylenearylene having 13 to 16 carbon atoms, and in which R 4 is an olefinically unsaturated copolymerizable radical having 2 to 24 carbon atoms.
17. An ink of claim 16 , wherein R 4 is an olefinically unsaturated copolymerizable radical having 2 to 8 carbon atoms.
18. An ink of claim 1 , wherein the ink has a good transferability from a mold for making the contact lens to the contact lens.
19. An ink of claim 1 , wherein the ink is stable for at least 4 hours.
20. An ink of claim 19 , wherein the ink is stable for at least 24 hours.
21. An ink of claim 20 , wherein the ink is stable for at least three weeks.
22. An ink of claim 21 , wherein said crosslinkable poly(vinyl alcohol) is crosslinked by exposure to UV radiation.
23. A method for making a colored contact lens comprising the steps of:
(a) coating at least a portion of at least one lens-forming surface of a lens mold with a water-based ink comprising water; a colorant; and a binder polymer which is a crosslinkable, water-soluble poly(vinyl alcohol) having olefinically unsaturated radicals, provided that the ink does not include a cross linker to crosslink two or more monomers or polymer molecules, wherein the ink has a viscosity of greater than 100 centipoise, wherein the ink without crosslinker has good adhesion to a medical device, wherein the water-soluble poly(vinyl alcohol) is a crosslinkable polymer based on a polyhydroxyl compound which is a derivative of a poly(vinyl alcohol) having a molecular weight of at least about 2000 which comprises from about 0.5 to about 80%, based on the number of hydroxyl groups in the poly(vinyl alcohol), of units of the formula I, I and II, I and III, or I and II and III
in which R is alkylene having up to 12 carbon atoms, R 1 is hydrogen or lower alkyl, R 2 is an olefinically unsaturated, electron-withdrawing, crosslinkable radical, preferably having up to 25 carbon atoms, and R 3 is hydrogen, a C 1 -C 6 alkyl group or a cycloalkyl group,
wherein R and R 3 are as defined for formula I above, and R 7 is a primary, secondary or tertiary amino group or a quaternary amino group of the formula N + (R′) 3 X − , in which each R′, independently of the others, is hydrogen or a C 1 -C 4 alkyl radical and X is a counter ion,
in which R and R 3 are as defined for formula I above, and R 8 is the radical of a monobasic, dibasic or tribasic, saturated or unsaturated, aliphatic or aromatic organic acid or sulfonic acid;
(b) adding a lens forming composition to the lens mold while maintaining the color coat in position; and
(c) curing the lens-forming composition to form a coated lens;
wherein said contact lens is characterized by having no visible observation of colorant bleeding, smearing, or delamination after digitally rubbing said contact lens between either two fingers or a finger and a palm for approximately 10 seconds.