Transparent polycrystalline yttrium aluminum garnet
View Patent ↗A transparent polycrystalline yttrium aluminum garnet (YAG) ceramic is described wherein the ceramic is colorless and transparent in both as-sintered and post-sinter, air-fired states which makes it highly desirable for lamp applications. The transparent YAG ceramic is co-doped with an amount of MgO and an amount of ZrO 2 wherein the weight ratio of MgO to ZrO 2 is from about 1.5:1 to 3:1.
1. A transparent, sintered ceramic material comprising a polycrystalline yttrium aluminum garnet containing an amount of MgO and an amount ZrO 2 wherein the weight ratio of MgO to ZrO 2 is from about 1.5:1 to about 3:1.
2. The ceramic material of claim 1 wherein the weight ratio of MgO to ZrO 2 is about 2:1.
3. The ceramic material of claim 1 wherein the amount of MgO ranges from about 200 to about 1000 ppm by weight and the amount of ZrO 2 ranges from about 70 to about 660 ppm by weight.
4. The ceramic material of claim 1 wherein the amount of MgO ranges from about 200 to about 500 ppm by weight and the amount of ZrO 2 ranges from about 70 to about 330 ppm by weight.
5. The ceramic material of claim 1 wherein the amount of MgO is about 350 ppm by weight and the amount of ZrO 2 is about 187 ppm by weight.
6. The ceramic material of claim 1 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 93% and an in-line transmittance of at least 10% at 600 nm.
7. The ceramic material of claim 1 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 96% and an in-line transmittance of at least 30% at 600 nm.
8. A transparent, sintered ceramic material comprising polycrystalline yttrium aluminum garnet co-doped with MgO and ZrO 2 , the ceramic material being colorless and transparent in both an as-sintered state and a post-sinter, air-fired state.
9. The ceramic material of claim 8 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 93% and an in-line transmittance of at least 10% at 600 nm in both states.
10. The ceramic material of claim 8 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 96% and an in-line transmittance of at least 30% at 600 nm in both states.
11. The ceramic material of claim 8 wherein the post-sinter, air-fired state comprises firing the as-sintered ceramic in air at 1000-1350° C. for 2 hours.
12. The ceramic material of claim 11 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 93% and an in-line transmittance of at least 10% at 600 nm in both states.
13. The ceramic material of claim 11 wherein the ceramic material at about an 0.8 mm thickness has a total transmittance between 400-700 nm of at least 96% and an in-line transmittance of at least 30% at 600 nm in both states.