Oxidation resistant ferritic stainless steels
View Patent ↗A method for making a ferritic stainless steel article having an oxidation resistant surface includes providing a ferritic stainless steel comprising aluminum, at least one rare earth metal and 16 to less than 30 weight percent chromium, wherein the total weight of rare earth metals is greater than 0.02 weight percent. At least one surface of the ferritic stainless steel is modified so that, when subjected to an oxidizing atmosphere at high temperature, the modified surface develops an electrically conductive, aluminum-rich, oxidation resistant oxide scale comprising chromium and iron and a having a hematite structure differing from Fe 2 O 3 , alpha Cr 2 O 3 and alpha Al 2 O 3 . The modified surface may be provided, for example, by electrochemically modifying the surface, such as by electropolishing the surface.
1. A method for making a ferritic stainless steel article having an oxidation resistant surface, the method comprising:
providing a ferritic stainless steel comprising 0.2 to 1.0 weight percent aluminum, 16 to less than 30 weight percent chromium, and at least one rare earth metal selected from the group consisting of cerium, lanthanum, and praseodymium, wherein the total weight of rare earth metals is from 0.02 to 1.0 weight percent; and
electropolishing at least one exposed surface of the ferritic stainless steel,
so that, when subjected to an oxidizing atmosphere at high temperature, the exposed electropolished surface develops an electrically conductive, aluminum-rich, oxidation resistant oxide scale comprising chromium and iron and having a hematite structure differing from Fe 2 O 3 , alpha Cr 2 O 3 , and alpha Al 2 O 3 .
2. The method of claim 1 , wherein lattice parameters a o and c o of the oxide scale differ from a o and c o of Fe 2 O 3 , alpha Cr 2 O 3 , and alpha Al 2 O 3 .
3. The method of claim 1 , wherein the at least one exposed electropolished surface develops the oxide scale when heated in an oxidizing atmosphere at a temperature in the range of 750° C. to 850° C.
4. The method of claim 1 , wherein the at least one exposed electropolished surface develops the oxide scale when heated in an oxidizing atmosphere for at least 100 hours at a temperature in the range of 750° C. to 850° C.
5. The method of claim 1 , wherein the oxide scale is characterized by lattice parameters a o in the range of 4.95 to 5.04 Å and c o in the range of 13.58 to 13.75 Å.
6. The method of claim 1 , wherein the oxide scale is characterized by nominal lattice parameters a o =4.98 Å and c o =13.57 Å.
7. The method of claim 1 , wherein the exposed electropolished surface develops the oxide scale when heated in an oxidizing atmosphere for at least 100 hours at a temperature in the range of 750° C. to 850° C., and wherein the oxide scale is characterized by a o in the range of 4.95 to 5.04 Å and c o in the range of 13.58 to 13.75 Å.
8. A method for making a ferritic stainless steel article having at least one oxidation resistant surface, the method comprising:
providing a ferritic stainless steel comprising 0.2 to 1.0 weight percent aluminum, 16 to less than 30 weight percent chromium, and at least one rare earth metal selected from the group consisting of cerium, lanthanum, and praseodymium, wherein the total weight of rare earth metals is from 0.02 to 1.0 weight percent; and
electropolishing at least one exposed surface of the ferritic stainless steel,
so that the exposed electropolished surface develops an aluminum-rich oxide scale when heated in an oxidizing atmosphere for at least 100 hours at a temperature in the range of 750° C. to 850° C., the oxide scale comprising iron and chromium and having a hematite structure, a o in the range of 4.95 to 5.04 Å, and c o in the range of 13.58 to 13.75 Å.
9. A method for making a ferritic stainless steel article having at least one oxidation resistant surface, the method comprising:
electropolishing at least one exposed surface of a ferritic stainless steel comprising 0.4 to 0.8 weight percent aluminum, 18 to 22 weight percent chromium, and 0.02 to 0.2 weight percent rare earth metals, wherein the rare earth metals are selected from the group consisting of cerium, lanthanum, praseodymium, and combinations of any thereof;
wherein the electropolishing chemically modifies the at least one exposed surface of the ferritic stainless steel so that the electropolished exposed surface develops an aluminum-rich oxide scale when heated in an oxidizing atmosphere at a temperature in the range of 750° C. to 850° C., the aluminum-rich oxide scale comprising iron and chromium and having a hematite structure, a o in the range of 4.95 to 5.04 Å, and c o in the range of 13.58 to 13.75 Å.
10. The method of claim 9 , further comprising heating the ferritic stainless steel article in an oxidizing atmosphere at a temperature in the range of 750° C. to 850° C., wherein the exposed electropolished surface develops an aluminum-rich oxide scale comprising iron and chromium and having a hematite structure, a o in the range of 4.95 to 5.04 Å, and c o in the range of 13.58 to 13.75 Å.
11. The method of claim 9 , wherein the electropolishing decreases the rate of oxidation of the ferritic stainless steel by at least one order of magnitude when compared to a non-electropolished sample of the same ferritic stainless steel, when heated in an oxidizing atmosphere at a temperature in the range of 750° C. to 850° C.