View Patent ↗A nonaqueous-electrolyte battery which is capable of preventing introduction of water and deterioration in the capacity thereof is disclosed. The nonaqueous-electrolyte battery according to the present invention incorporates a case constituted by laminated films; and a unit cell which is accommodated in the case and having a structure that the peripheries of the case is sealed with heat, wherein when an assumption is made that the quantity of water capable of penetrating a heat-weld resin layer which is the innermost layer of the case having a thickness of T (μm) is R (g/m 2 ·day), the cross sectional area of resin in a heat-sealed portion is S (cm 2 ), an average width of the heat-sealed portion is W (cm) and the capacity of the unit cell is C (Wh), the following relationship is satisfied: (T×R×S)/(W×C)≦0.96 μg/Wh·day. When the foregoing structure is employed, water introducing rate can be reduced to 350 μg/year or lower per capacity (Wh).
1. A nonaqueous-electrolyte battery comprising:
a unit cell with a capacity (C); and
a case accommodating the unit cell, said case comprising at least one plastic film layer A; said case being folded along a plane such that A faces itself thereby forming an opposing section A′; said unit cell being disposed between A and A′; a portion of A and A′ being heat-sealed together along at least a portion of a periphery of said accommodated unit cell; said heat sealed-portion of said case having a thickness (D) of from 20 μm to 200 μm, a moisture vapor permeability (R) as measured on a plastic film layer of thickness (T), an inner peripheral sealing length (L), a cross-sectional area (S) calculated as D×L, and an average heat-sealed portion width (W) of 2 mm to 5 mm;
wherein said case has a water penetration rate, as calculated by (T×R×S)/(W×C), of less than 0.96 μg per day per unit capacity of said battery.
2. The nonaqueous-electrolyte battery according to claim 1 , wherein said plastic film layer A comprises a polyolefin resin.
3. The nonaqueous-electrolyte battery according to claim 2 , wherein the polyolefin resin is selected from the group consisting of polypropylene, polyethylene, denatured polypropylene, denatured polyethylene, and mixtures thereof.
4. The nonaqueous-electrolyte battery according to claim 1 , wherein the cell comprises a gel or solid electrolyte which contains a matrix polymer and lithium salt.
5. The nonaqueous-electrolyte battery according to claim 1 , wherein the cell comprises a negative electrode that contains a negative electrode active material which is capable of doping and dedoping lithium.
6. The nonaqueous-electrolyte battery according claim 5 , wherein the negative electrode active material comprises material a carbon material.
7. The nonaqueous-electrolyte battery according claim 1 , wherein the cell comprises a positive electrode that contains a positive electrode composite oxide of lithium and a transition metal.
8. The nonaqueous-electrolyte battery according claim 1 , wherein said thickness (D) of said heat-sealed portion of said case is from 20 μm to 70 μm.
9. The nonaqueous-electrolyte battery according claim 1 , wherein said moisture vapor permeability R is 20 gm −2 d −1 , as measured at thickness T of 20 μm.
10. The nonaqueous-electrolyte battery according claim 1 , wherein said capacity C of said unit cell is 2 Wh.
11. The nonaqueous-electrolyte battery according claim 1 , wherein said unit cell retains at least 87% capacity after storage for one year at 23° C. and 55% relative humidity.
12. The nonaqueous-electrolyte battery according claim 1 , wherein said case has a water penetration rate, as calculated by (T×R×S)/(W×C), of less than 0.88 μg per day per unit capacity of said battery.
13. The nonaqueous-electrolyte battery according claim 1 , wherein said case has a water penetration rate, as calculated by (T×R×S)/(W×C), of less than 0.56 μg per day per unit capacity of said battery.
14. The nonaqueous-electrolyte battery according claim 1 , wherein said case has a water penetration rate, as calculated by (T×R×S)/(W×C), of less than about 0.34 μg per day per unit capacity of said battery.
15. The nonaqueous-electrolyte battery according claim 1 , wherein said case comprises at least two plastic film layers A and B bonded to a metal film layer such that the metal film layer is sandwiched between A and B and thickness (D) is measured as a distance between opposing portions of the metal film layer.
16. A nonaqueous-electrolyte battery comprising:
a unit cell with a capacity (C); and
a case accommodating the unit cell, said case comprising at least two plastic film layers A and B bonded to a metal film layer such that the metal film layer is sandwiched between A and B; said case being folded along a plane such that A faces itself thereby forming an opposing section A′; said unit cell being disposed between A and A′; a portion of A and A′ being heat-sealed together along at least a portion of a periphery of said accommodated unit cell; said heat sealed-portion of said case having a thickness (D) of from 20 μm to 70 μm measured as a distance between opposing portions of the metal film layer, a moisture vapor permeability (R) of 20 gm −2 d −1 as measured on a plastic film layer with thickness (T) of 20 μm, an inner peripheral sealing length (L), a cross-sectional area (S) calculated as D×L, and an average heat-sealed portion width (W) of 2 mm to 5 mm;
wherein said case has a water penetration rate, as calculated by (T×R×S)/(W×C), of less than about 0.96 μg per day per unit capacity of said battery and said unit cell retains at least 87% capacity after storage for one year at 23° C. and 55% relative humidity.