Solid electrolyte composite for electrochemical reaction apparatus
View Patent ↗A solid polymer electrolyte composite for an electrochemical reaction apparatus that possesses satisfactory ion conduction properties and has excellent mechanical strength and heat resistance, is provided. the solid polymer electrolyte composite is characterized in that a solid polymer electrolyte is contained in the continuous pores of an expanded porous polytetrafluoroethylene sheet which has continuous pores and in which the inner surfaces defining the pores are covered with a functional material such as a metal oxide. An electrochemical reaction apparatus containing an electrolyte, wherein said electrochemical reaction apparatus is characterized in that the aforementioned solid polymer electrolyte composite is used as this electrolyte is also provided.
1. An integral, substantially air impermeable polymeric membrane for use in an electrochemical apparatus or process comprising:
a) a polymeric sheet comprising polymer and having a porous structure with a microstructure of nodes and fibrils and an interior volume of said porous structure between the nodes and fibrils,
b) the polymeric sheet having distributed in the nodes and fibrils of the polymeric sheet:
i) metal;
ii) an organic polymer; or
iii) a combination thereof, and
c) said interior volume of said porous structure comprising a porosity of the polymeric sheet of greater than 35% and being substantially occluded by an ion-exchange resin to provide ionic conductance for use in the electrochemical apparatus or process.
2. The membrane of claim 1 wherein the polymeric sheet has distributed therein a precious metal.
3. An integral, substantially air impermeable polymeric membrane for use in an electrochemical apparatus or process comprising:
a) a polymeric sheet comprising polymer and having a porous structure with a microstructure of nodes and fibrils and an interior volume of the porous structure between the nodes and fibrils,
b) fumed silica distributed in the nodes and fibrils of the polymeric sheet, and
c) electrolyte substantially occluding said interior volume of said porous structure to provide ionic conductance for use in the electrochemical apparatus or process.
4. The membrane of claim 1 wherein the polymeric sheet has distributed therein titania.
5. The membrane of claim 1 wherein the polymeric sheet has distributed therein platinum.
6. The membrane of claim 1 wherein the polymeric sheet has distributed therein platinum supported on a substrate.
7. A polymeric membrane for use in an electrochemical apparatus or process comprising:
a) a polymeric sheet comprising polymer and having a porous structure with a microstructure of nodes and fibrils and an interior volume between the nodes and fibrils,
b) the polymeric sheet having distributed in the nodes and fibrils:
i) metal;
ii) an organic polymer; or
iii) a combination thereof, and
c) said interior volume of said porous structure is substantially occluded by an ion-exchange resin to provide ionic conductance for use in the electrochemical apparatus or process,
wherein the polymeric sheet is expanded porous PTFE.
8. The membrane of claim 1 , wherein the polymeric sheet has metal distributed therein.
9. The membrane of claim 1 , wherein the polymeric sheet has an organic polymer distributed therein.
10. The membrane of claim 1 , wherein the polymeric sheet has a thickness of less than 50 microns.
11. The membrane of claim 1 , wherein the membrane is disposed between two fuel cell electrodes.
12. The membrane of claim 11 , wherein the polymeric sheet has a thickness of less than 38 microns, and wherein the membrane that is disposed between said two electrodes of a fuel cell provides a steady state current of at least 1.78 amps/cm 2 at 0.5 volts, with no humidification of incoming fuel cell air and hydrogen reactants, with air and hydrogen feed both at 40 psig and 25° C., and the fuel cell temperature at 50° C.
13. The membrane of claim 1 , wherein said ion-exchange resin is fluorinated.
14. The membrane of claim 10 , wherein the polymeric sheet has a thickness between 13 microns and 50 microns.
15. The polymeric membrane of claim 1 in which the polymeric sheet comprises a porous polymeric film; and the ion exchange resin is a polymer different from the polymeric film.
16. The polymeric membrane of claim 1 in which said interior volume of said porous structure comprises a porosity of the polymeric sheet comprises a porosity of the polymeric sheet of 40% to 95%.
17. The polymeric membrane of claim 1 in which said interior volume of said porous structure comprises a porosity of the polymeric sheet comprises a porosity of 70% to 95%.
18. The polymeric membrane of claim 1 in which the polymeric sheet comprises an expanded porous PTFE film having substantially fibrils with substantially no nodes present.