Bentonite nodules
View Patent ↗Compressed bentonite-containing nodules are disclosed as are methods for their production and methods for using them to plug wells.
1. A method for forming a material for plugging a well comprising
a. obtaining a feedstock comprising bentonite in admixture with a proportion of water to permit the formation of compacted nodules having a density of at least 2.0 g/cm 3 and a mean particle survival at a crush force of at least 800 newtons and capable of having at least 50% survival when dropped 1.5 meters onto a concrete surface,
b. feeding the feedstock under pressure to a continuous roll press machine under conditions to permit the formation of said compacted nodules and
c. recovering the compacted nodules.
2. The method of claim 1 wherein the feedstock comprises
from about 35% to about 98% by weight bentonite,
from about 0% to about 45% by weight nonbentonite solids, and
from about 2% to about 20% by weight nonconnate water.
3. The method of claim 1 wherein the feedstock comprises
from about 45% to about 95% by weight bentonite,
from about 0% to about 35% by weight nonbentonite solids, and
from about 5% to about 20% by weight nonconnate water.
4. The method of claim 1 wherein the feedstock comprises
from about 64% to about 88% by weight bentonite,
from about 0% to about 20% by weight nonbentonite solids, and
from about 12% to about 16% by weight nonconnate water.
5. The method of claim 1 wherein the feedstock consists essentially of
from about 85% to about 90% by weight bentonite and
from about 10% to about 15% by weight nonconnate water.
6. The method of claim 1 wherein the pressure is a pressure of at least about 1 Mpa.
7. The method of claim 1 wherein the pressure is a pressure of at least about 3 Mpa.
8. The method of claim 1 wherein the pressure is a pressure of at least about 5 Mpa.
9. The method of claim 1 wherein said roller press is operated at a speed of from about 2 RPM to about 50 RPM.