Superabsorbent polymer with slow absorption times
View Patent ↗The invention relates to hydrophilic superabsorbent polymer comprising a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % of internal crosslinking agent; c) from about 0.001 to about 5.0 wt. % of surface crosslinking agent applied to the particle surface; and d) wherein the composition has a degree of neutralization of more than about 20%, and from about 20 mole % to about 75 mole % of the unsaturated acid group containing monomers are neutralized with a first neutralizing agent, and from about 5 mole % to about 40 mole % of the unsaturated acid group containing monomers are neutralized with a second neutralizing agent; at a temperature of about 75° C. or less. Such hydrophilic superabsorbent polymers have an Absorption Time of about 5+10 a 2 minutes or greater, where a is the mean particle size of the superabsorbent material in millimeters, a capacity of about 15 g/g or greater, a Drop Penetration Value of about 2 seconds or less, and a floatability of 50% or less.
1. A hydrophilic superabsorbent polymer composition comprising an absorbent polymer that is the reaction product of:
a) from about 55 to about 99.9 wt. % based on the absorbent polymer of polymerizable unsaturated acid group containing monomers;
b) a first neutralizing agent selected from monovalent hydroxides, monovalent carbonate, or monovalent bicarbonate salts, or mixtures thereof;
c) a second neutralizing agent comprising a multivalent metal hydroxide;
d) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; and
e) an initiator for initiation of free-radical polymerization;
wherein the absorbent polymer has a degree of neutralization of more than about 25%, and from about 20 mole % to about 75 mole % of the unsaturated acid group containing monomers are neutralized with the first neutralizing agent, and from about 5 mole % to about 40 mole % of the unsaturated acid group containing monomers are neutralized with the second neutralizing agent, at a temperature of about 75° C. or less, and the absorbent polymer is formed into an absorbent polymer particle which is surface treated with
from about 0.001 to about 5.0 wt. % of surface crosslinking agent applied to the polymer particle surface; and
wherein the hydrophilic superabsorbent polymer composition has an absorption time of about 5+10 a 2 minutes or greater, where a is the mean particle size of the superabsorbent material in millimeters, a liquid capacity of about 15 g/g or greater, a drop penetration value of about 2 seconds or less, and a floatability of about 50% or less.
2. The hydrophilic superabsorbent polymer composition of claim 1 having a liquid capacity of about 20 g/g or greater.
3. The hydrophilic superabsorbent polymer composition of claim 1 having a liquid capacity of about 25 g/g or greater.
4. The hydrophilic superabsorbent polymer composition of claim 1 having an Absorption Time of about 7+10 a 2 minutes or greater.
5. The hydrophilic superabsorbent polymer composition of claim 1 having an Absorption Time of about 10+10 a 2 minutes or greater.
6. The hydrophilic superabsorbent polymer composition of claim 1 having a Gel Bed Permeability of about 20×10 −9 cm 2 or greater.
7. The hydrophilic superabsorbent polymer composition of claim 1 having a Gel Bed Permeability of about 50×10 −9 cm 2 or greater.
8. The hydrophilic superabsorbent polymer composition of claim 1 having a Gel Bed Permeability of about 80×10 −9 cm 2 or greater.
9. The hydrophilic superabsorbent polymer composition of claim 1 wherein the first neutralizing agent is sodium hydroxide, and the second neutralizing agent is selected from calcium hydroxide or magnesium hydroxide.
10. The hydrophilic superabsorbent polymer composition of claim 1 wherein at least 40% of the neutralization is accomplished by the first neutralizing agent.
11. The hydrophilic superabsorbent polymer composition of claim 1 wherein the first neutralizing agent comprises a monovalent metal hydroxide.
12. A water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition having a degree of neutralization of more than about 25%, wherein the hydrophilic superabsorbent polymer composition comprises an absorbent polymer that is the reaction product of polymerizable unsaturated acid group containing monomers, an internal crosslinking agent, and an initiator for initiation of free-radical polymerization; wherein from about 20 mole % to about 75 mole % of the unsaturated acid group containing monomers are neutralized with a first neutralizing agent selected from monovalent hydroxide, monovalent carbonate or bicarbonate salts, or mixtures thereof, and from about 5 mole % to about 40 mole % of the unsaturated acid group containing monomers are neutralized with a second neutralizing agent comprising a multivalent metal hydroxide; wherein the hydrophilic superabsorbent polymer composition has an absorption time of about 5+10 a 2 minutes or greater, where a is the mean particle size of the superabsorbent material in millimeters, a liquid capacity of about 15 g/g or greater, a drop penetration value of about 2 seconds or less, and a floatability of about 50% or less.
13. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having a liquid capacity of about 20 g/g or greater.
14. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having a liquid capacity of about 25 g/g or greater.
15. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having an Absorption Time of about 7+10 a 2 minutes or greater.
16. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having an Absorption Time of about 10+10 a 2 minutes or greater.
17. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having a Gel Bed Permeability of about 20×10 −9 cm 2 or greater.
18. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having a Gel Bed Permeability of about 50×10 −9 cm 2 or greater.
19. The water insoluble, cross-linked, partially neutralized, hydrophilic, superabsorbent polymer composition of claim 12 having a Gel Bed Permeability of about 80×10 −9 cm 2 or greater.
20. A hydrophilic superabsorbent polymer composition comprising an absorbent polymer that is the reaction product of:
a) from about 55 to about 99.9 wt. % based on the absorbent polymer of polymerizable unsaturated acid group containing monomers;
b) a first neutralizing agent selected from monovalent hydroxides, monovalent carbonate or bicarbonate salts, or mixtures thereof;
c) a second neutralizing agent comprising a multivalent metal hydroxide;
d) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; and
e) an initiator for initiation of free-radical polymerization;
wherein the absorbent polymer has a degree of neutralization of more than about 25%, and from about 20 mole % to about 75 mole % of the unsaturated acid group containing monomers are neutralized with the first neutralizing agent, and from about 5 mole % to about 40 mole % of the unsaturated acid group containing monomers are neutralized with the second neutralizing agent, and the absorbent polymer is formed into a absorbent polymer particle which is surface treated with
from about 0.001 to about 5.0 wt. % of surface crosslinking agent applied to the particle surface.
21. The hydrophilic superabsorbent polymer composition of claim 20 wherein at least 40% of the neutralization is accomplished by the first neutralizing agent.
22. The hydrophilic superabsorbent polymer composition of claim 20 wherein the first neutralizing agent comprises a sodium hydroxide, and the second neutralizing agent is selected from calcium hydroxide or magnesium hydroxide.