Patching resins for insulating tapes
View Patent ↗The present invention comprises a polymeric epoxy patching resin containing metal intercalated AlSiO structures. The AlSiO structures are typically nanoclays, and the preferred metals are Cr, Sn and Zn, and mixtures thereof. The patching resin is applied to damaged mica tapes, where the metal intercalated nanoclays penetrate the damaged area, leaving a homogenous patch. The present invention may also be used to thicken an area of insulating tape.
1. A method for repairing a damaged area in an insulation material comprising:
formulating a patching resin comprising a resinous composition, metal intercalated AlSiO nano structures, and a reactive diluent, wherein the ratio of said metal intercalated AlSiO nano structures to said resinous composition and said reactive diluent is between 3-35% wt;
applying said patching resin to said damaged area; and
curing said patching resin to produce a patch;
wherein said patching resin has a voltage endurance of at least 1000 hours at 188 volts/mil (7.5 kv/mm);
wherein the viscosity of said patching resin is between 100-300 cps; and
wherein said metal intercalated AlSiO nano structures penetrate said damaged area of said mica insulation material creating a substantially homogenous transition between said damaged area and said patch.
2. The method of claim 1 , wherein the ratio of said metal intercalated AlSiO nano structures to said resinous composition and said reactive diluent is between 5-10% wt.
3. The method of claim 1 , wherein the curing of said patching resin is performed locally on said damaged area.
4. The method of claim 1 , wherein the temperature of the curing of said patching resins is between about 60-120° C.
5. The method of claim 1 , wherein the temperature of the curing of said patching resins is approximately 90° C.
6. The method of claim 1 , wherein the metal in said metal intercalated AlSiO nano structures is one of Cr, Sn, Zn and mixtures thereof.
7. The method of claim 1 , wherein the AlSiO nano structures in said metal intercalated AlSiO nano structures are nanoclays.
8. The method of claim 1 , wherein said resinous composition is bisphenol F.
9. The method of claim 1 , wherein said reactive diluent is at least one of DGENPG, DGEBD and mixtures thereof.
10. The method of claim 1 , wherein the viscosity of said patching resin is between 120-175 cps.
11. The method of claim 1 , wherein said patching resin has a voltage endurance of 2800 to 3000 hours at 188 volts/mil (7.5 kv/mm).
12. A method for repairing a damaged area in a mica insulation material comprising:
formulating a patching resin comprising a resinous composition, metal intercalated AlSiO nano structures, and a reactive diluent, wherein the ratio of said metal intercalated AlSiO nano structures to said resinous composition and said reactive diluent is between 3-35% wt;
applying said patching resin to said damaged area; and
curing said parching resin with a localized heat on said damaged area of between 60-120° C.;
wherein said patching resin has a voltage endurance of at least 1000 hours at 188 volts/mil (7.5 kv/mm);
wherein said metal intercalated AlSiO nano structures are substantially free of solvent when formulating said patching resin;
wherein the viscosity of said patching resin is between 100-300 cps;
wherein said metal intercalated AlSiO nano structures penetrate said damaged area of said mica insulation material creating a substantially homogenous transition between said damaged area and said patch;
wherein the metal in said metal intercalated AlSiO nano structures is one of Cr, So, Zn and mixtures thereof.
13. A method of thickening an insulating tape comprising
formulating a patching resin comprising a resinous composition, metal intercalated AlSiO nano structures, and a reactive diluent, wherein the ratio of said metal intercalated AlSiO nano structures to said resinous composition and said reactive diluent is between 3-35% wt;
applying said patching resin to said insulating tape;
wherein said patching resin has a voltage endurance of at least 1000 hours at 188 volts/mil (7.5 kv/mm);
wherein the viscosity of said patching resin is between 100-300 cps;
wherein said metal intercalated AlSiO nano structures penetrate said insulating tape creating a substantially homogenous transition between said insulating tape and said patching resin; and
curing said patching resin to produce a thicker insulating tape.
14. The method of claim 13 , wherein the ratio of said metal intercalated AlSiO nano structures to said resinous composition and said reactive diluent is between 5-10% wt.
15. The method of claim 13 , wherein the curing of said patching resin is performed locally on said damaged area.
16. The method of claim 13 , wherein the temperature of the curing of said patching resins is between about 60-120° C.
17. The method of claim 13 , wherein the metal in said metal intercalated AlSiO nano structures one of Cr, Sn, Zn and mixtures thereof.
18. The method of claim 13 , wherein the AlSiO nano structures in said metal intercalated AlSiO nano structures are nanoclays.
19. The method of claim 13 , wherein said resinous composition is bisphenol F.
20. The method of claim 13 , wherein said reactive diluent is at least one of DGENPG, DGEBD and mixtures thereof.
21. The method of claim 13 , wherein the viscosity of said patching resin is between 120-175 cps.
22. The method of claim 13 , wherein said metal intercalated AlSiO nano structures are substantially free of solvent when formulating said patching resin.
23. The method of claim 13 , wherein said patching resin has a voltage endurance of 2800 to 3000 hours at 188 volts/mil (7.5 ky/mm).