Fire retardant intumescent coating
View Patent ↗A fire retardant intumescent coating composition comprises: (a) 30 to 60% by weight of a phosphorous containing material which decomposes to produce phosphoric acid when the coating is exposed to fire; (b) 10 to 30% by weight of a thermosetting binder; (c) 2.5 to 10% by weight of a curing agent for the thermosetting binder; and (d) 5 to 40% by weight of a thermoplastic binder, wherein the active groups of the thermosetting and thermoplastic binders are chosen so as to impart charring and blowing functions to the intumescent coating composition. The thermosetting binder is advantageously a hydroxylated thermosetting binder, suitably an epoxy resin. The thermoplastic binder is advantageously an oxygenated heterocyclic thermoplastic binder, suitably an aldehyde and/or ketone resin. The coating composition may contain 1 to 10% by weight of a colouring agent, suitably titanium dioxide. The coating composition may contain 0.1 to 10% by weight of melt viscosity modifier, suitably hydrogenated castor oil.
1. A fire retardant intumescent coating composition selected from the group consisting of powder coating compositions and, aqueous coating compositions, said composition comprising:
(a) 30 to 60% by weight of a phosphorous containing material which decomposes to produce phosphoric acid when the coating is exposed to fire;
(b) 10 to 30% by weight of a thermosetting binder;
(c) 2.5 to 10% by weight of a curing agent for the thermosetting binder; and
(d) 5 to 40% by weight of a thermoplastic binder,
wherein each of the thermosetting and thermoplastic binders comprise groups that react with the said phosphoric acid, thereby imparting charring and blowing functions to the intumescent coating composition.
2. A fire retardant intumescent coating composition according to claim 1 wherein the total weight of the said thermosetting and thermoplastic binder accounts for 30% or more by weight of the composition.
3. A fire retardant intumescent coating composition according to claim 1 wherein the phosphorous containing material is a sodium, potassium or ammonium polyphosphate.
4. A fire retardant intumescent coating composition according to claim 1 wherein the thermosetting binder is a hydroxylated thermosetting resin.
5. A fire retardant intumescent coating composition according to any one of claims 1 to 4 wherein the thermosetting binder is an epoxy resin.
6. A fire retardant intumescent coating composition according to claim 1 wherein the curing agent for the thermosetting binder is a phenolic curing agent.
7. A fire retardant intumescent composition according to claim 1 wherein the thermoplastic binder is an aldehyde or ketone resin.
8. A fire retardant intumescent coating composition according to claim 1 containing 0.1 to 10% by weight of a melt viscosity modifier.
9. A fire retardant intumescent coating composition according to claim 8 wherein the melt viscosity modifier is hydrogenated castor oil.
10. A fire retardant intumescent coating composition according to claim 1 containing 1 to 10% by weight of a colouring agent.
11. A fire retardant intumescent coating composition according to claim 10 wherein the colouring agent is titanium dioxide.
12. A fire retardant intumescent coating composition according to claim 1 containing one or more additives selected from the group consisting of a china clay, melamine phosphate, vitriflers, metal salts and melamine.
13. A fire retardant intumescent powder coating composition as claimed in claim 1
further wherein, the said composition is made by a process comprising premixing the said components (a)–(d), extruding the premix, and grinding the thus formed extrudate to form a powder.
14. A composition according to claim 13 wherein the thermoplastic binder is an oxygenated heterocyclic thermoplastic resin.
15. A composition according to claim 14 wherein the thermoplastic resin is an aldehyde or ketone resin.