Joint construction of cobalt-based alloy
View Patent ↗In the joint construction of cobalt-based alloy, a cobalt-based alloy layer 1 , in which granular or massive eutectic carbide 2 disperses, is joined to a metal of a base metal 37 via an insert metal layer 36 . For the joint construction of cobalt-based alloy, liquid phase diffusion bonding is performed at a temperature of 1100° C. for a retention time of 1 hour with an insert metal with a thickness of about 40 μm being interposed between the base metal, which is S45C carbon steel, and a cobalt-based alloy material which has granular or massive eutectic carbide with a grain size not larger than 30 μm in a matrix of cast structure and contains 1.03 wt % C, 29.73 wt % Cr, 3.86 wt % W, 2.59 wt % Ni, 2.67 wt % Fe, 0.59 wt % Si, and 0.07 wt % Mo, the balance substantially being Co. The cobalt-based alloy layer 1 after bonding contains granular or massive eutectic carbide.
1. A valve comprising a valve casing and a valve element disposed in said valve casing, said valve casing having a valve seat which comes into contact with said valve element, wherein
said valve seat has a cobalt-based alloy portion in which granular or massive eutectic carbide disperses in a matrix of metal microstructure and which is brought into contact with said valve element, and a body portion installed to said valve casing,
said cobalt-based alloy portion is diffusion bonded to said body portion by interposing an insert metal between said cobalt-based alloy portion and said body portion, and
a layer of said insert metal is formed over said body portion, and said cobalt-based alloy portion is located over said insert metal layer.
2. A valve comprising a valve casing and a valve element disposed in said valve casing, said valve casing and said valve element each having a valve seat which comes into contact with each other, wherein
said valve seats each have a cobalt-based alloy portion in which granular or massive eutectic carbide disperses in a matrix of metal microstructure and which is brought into contact with the other valve element, and a body portion installed to said valve casing,
said cobalt-based alloy portion is diffusion bonded to said body portion by interposing an insert metal between said cobalt-based alloy portion and said body portion, and
a layer of said insert metal is formed over said body portion, and said cobalt-based alloy portion is located over said insert metal layer.
3. The valve according to claim 2 , wherein the grain size of said eutectic carbide is not larger than 30 μm.
4. The valve according to claim 2 , wherein said body portion is formed of carbon steel, low alloy steel, or stainless steel.
5. The valve according to claim 2 , wherein said cobalt-based alloy material portion contains 0.6 to 3% C, 2% or less Si, 25 to 32% Cr, 15% or less W, 0 to 3% Fe, 0 to 3% Ni, and 0 to 6% Mo by weight, the balance being Co and unavoidable impurities.
6. The valve according to claim 2 , wherein said insert metal layer contains an element diffused from said body portion and cobalt diffused from said cobalt-based alloy portion.
7. The valve according to claim 6 , wherein the grain size of said eutectic carbide is not larger than 30 μm.
8. The valve according to claim 6 , wherein said cobalt-based alloy material portion contains 0.6 to 3% C, 2% or less Si, 25 to 32% Cr, 15% or less W, 0 to 3% Fe, 0 to 3% Ni, and 0 to 6% Mo by weight, the balance being Co and unavoidable impurities.
9. The valve according to claim 6 , wherein said body portion is formed of carbon steel, low alloy steel, or stainless steel.
10. The valve according to claim 9 , wherein said cobalt-based alloy material portion contains 0.6 to 3% C, 2% or less Si, 25 to 32% Cr, 15% or less W, 0 to 3% Fe, 0 to 3% Ni, and 0 to 6% Mo by weight, the balance being Co and unavoidable impurities.
11. The valve according to claim 2 , wherein said body portion and said cobalt-based alloy portion contain an element diffused from said insert metal.
12. The valve according to claim 11 , wherein the grain size of said eutectic carbide is not larger than 30 μm.
13. The valve according to claim 11 , wherein said body portion is formed of carbon steel, low alloy steel, or stainless steel.
14. The valve according to claim 11 , wherein said cobalt-based alloy material portion contains 0.6 to 3% C, 2% or less Si, 25 to 32% Cr, 15% or less W, 0 to 3% Fe, 0 to 3% Ni, and 0 to 6% Mo by weight, the balance being Co and unavoidable impurities.
15. The valve according to claim 11 , wherein said insert metal layer contains an element diffused from said body portion and cobalt diffused from said cobalt-based alloy portion.
16. The valve according to claim 15 , wherein the grain size of said eutectic carbide is not larger than 30 μm.
17. The valve according to claim 15 , wherein said body portion is formed of carbon steel, low alloy steel, or stainless steel.
18. The valve according to claim 15 , wherein said cobalt-based alloy material portion contains 0.6 to 3% C, 2% or less Si, 25 to 32% Cr, 15% or less W, 0 to 3% Fe, 0 to 3% Ni, and 0 to 6% Mo by weight, the balance being Co and unavoidable impurities.