Low odor, light color, disposable article construction adhesive
View Patent ↗We have found a novel spray-on adhesive composition made from components including a high melt index polymer and a high melt tackifier that interact to produce a composition that can form a low odor, light color, non-tacky, hot melt adhesive material that can be used in disposable article manufacture. The adhesive is thermally stable at hot melt application conditions, is low in cost, is easily applied and produces high quality disposable articles.
1. A hot melt adhesive composition comprising:
(a) greater than about 40 wt % of an ethylene C 3 to C 18 α-olefin polymer composition comprising about 8 to 14 wt. % α-olefin having a melt index greater than 800 gm-10 min −1 ; and
(b) about 20 to 40 wt % of a hydrogenated hydrocarbon tackifying resin with a softening point greater than 125° C.;
wherein the weight ratio of the polymer composition to the resin is greater than about 1:1.
2. The composition of claim 1 , wherein the adhesive additionally comprises about 0.1 to 10 wt.-% of a block polymer and has a softening point of less than about 95° C.
3. The composition of claim 1 , wherein the polymer composition has a melt index greater then 9.950 gm-10 min −1 and the adhesive has a softening point of less than about 85° C.
4. The composition of claim 1 , wherein the weight ratio is greater than 1.5:1.
5. The composition of claim 1 , wherein the weight ratio is greater than 1.8:1.
6. The composition of claim 1 , wherein the tackifying resin has a softening point of about 127 to 145° C.
7. The adhesive of claim 1 , wherein polymer comprises is present in; the adhesive at a weight ratio of polymer:resin of at least 2:1.
8. The adhesive of claim 1 , wherein the ethylene/α-olefin polymer is present in an amount of at least about 60 wt-%.
9. The adhesive of claim 8 , wherein the ethylene/α-olefin polymer has a melt index greater than 950 gm-10 min −1 .
10. The adhesive of claim 8 , wherein the resin is present in the adhesive in an amount of 20 to 40 wt %.
11. The adhesive of claim 1 , wherein the ethylene/α-olefin polymer comprises a blend of a first ethylene/α-olefin polymer and a second ethylene/α-olefin polymer wherein the first has MI difference than the second.
12. The adhesive of claim 1 , wherein the adhesive consists essentially of greater than 40 wt % of ethylene/octene polymer composition comprising about 8 to 14 wt. % octane, the polymer having a melt index of about 850 to 1250 gm-10 min −1 and about 30 to 40 wt % of a hydrogenated hydrocarbon tackifying resin with a softening point greater than about 125° C.; wherein the weight ratio of the polymer to the resin is greater than about 1:1.
13. The adhesive of claim 1 wherein the adhesive has a viscosity of 2000 cPs to 10 5 cPs at 150° C. the adhesive has a softening point of less than about 85° C.
14. The adhesive of claim 1 wherein the adhesive has a viscosity of 4300 cPs to 7300 cPs at 150° C. and a and the adhesive has a softening point of less than about 95° C.