Aluminum-copper-magnesium alloys having ancillary additions of lithium
View Patent ↗An aluminum-copper-magnesium alloy having ancillary additions of lithium. The alloy composition includes from about 3 to about 5 weight percent Cu, from about 0.5 to about 2 weight percent Mg, and from about 0.01 to about 0.9 weight percent Li. The combined amount of Cu and Mg is maintained below a solubility limit of the aluminum alloy. The alloys possess improved combinations of fracture toughness and strength, and also exhibit good fatigue crack growth resistance.
1. An aluminum alloy comprising:
from about 3 to about 4.5 weight percent Cu,
from greater than 0.6 to about 2 weight percent Mg,
from about 0.01 to about 0.8 weight percent Li,
up to about 2.0 weight percent Zn,
up to about 2.0 weight percent Ag,
up to about 1 weight percent of a dispersoid, and
the balance aluminum and incidental elements and impurities,
Wherein the amount of Cu in the alloy is below the maximum solubility;
Wherein the amount of Mg in the alloy is below the maximum solubility; and
Wherein the fracture toughness and strength of the alloy are both increased when increasing lithium from about 0.01 to about 0.8 weight percent.
2. The aluminum ahoy of claim 1 , wherein the Li content of the alloy is from about 0.2 to about 0.8 weight percent.
3. The aluminum alloy of claim 1 , wherein the Li content of the alloy is from about 0.2 to about 0.7 weight percent.
4. The aluminum alloy of claim 1 , wherein the Cu content of the alloy is from about 3.5 to about 4.5 weight percent.
5. The aluminum alloy of claim 1 , wherein the Cu content of the alloy is from about 3.6 to about 4.4 weight percent.
6. The aluminum alloy of claim 1 , wherein the Mg content of the ahoy is from about 0.6 to about 1.5 weight percent.
7. The aluminum alloy of claim 1 , wherein the Mg content of the alloy is from about 0.7 to about 1.0 weight percent.
8. The aluminum alloy of claim 1 , wherein the Cu and Mg contents of the alloy conform to the formula:
Cu≦2-0.676 (Mg-6).
9. The aluminum alloy of claim 1 , wherein the Cu and Mg contents of the alloy conform to the formula:
Cu≦1.5-0.556 (Mg-6).
10. The aluminum alloy of claim 1 , wherein the Ag content of the alloy is from about 0.01 to about 2 weight percent.
11. The aluminum alloy of claim 10 , wherein the Ag content of the alloy is from about 0.05 to about 0.5 weight percent.
12. The aluminum alloy of claim 10 , wherein the Ag content of the alloy is from about 0.1 to about 0.4 weight percent.
13. The aluminum alloy of claim 1 , wherein the Zn content of the alloy is from about 0.05 to about 2 weight percent.
14. The aluminum alloy of claim 13 , wherein the Zn content of the alloy is from about 0.2 to about 1 weight percent.
15. The aluminum alloy of claim 13 , wherein the Zn content of the alloy is about 0.5 weight percent.
16. The aluminum alloy of claim 1 , further comprising from about 0.1 to about 2 weight percent Si.
17. The aluminum alloy of claim 1 , wherein said dispersoid is selected from at least one of the group consisting of chromium, vanadium, titanium, zirconium, manganese, nickel, iron, hafnium, and scandium.
18. The aluminum alloy of claim 17 , wherein the at least one dispersoid in the alloy is present in a total amount up to about 1.0 weight percent of the alloy.
19. The aluminum alloy of claim 1 , the alloy further comprising from about 0 to about 0.6 weight percent Mn.
20. The aluminum alloy of claim 1 , wherein the aluminum alloy is in the form of a plate.