Colloidal silica composition
View Patent ↗The invention relates to a method of producing a stable substantially aqueous silanized colloidal silica dispersion having a silica content of at least about 20 wt %, comprising mixing at least one silane compound and colloidal silica particles, wherein the weight ratio of silane to silica is from about 0.003 to about 0.2. The invention also relates to a dispersion obtainable by the method, and to a stable substantially aqueous silanized colloidal silica dispersion having a silica content of at least about 20 wt %, wherein the weight ratio of silane to silica is from about 0.003 to about 0.2. The invention further concerns the use of the dispersion for coatings applications and as an additive.
1. A method of producing a stable aqueous silanized colloidal silica dispersion without the presence of any water-miscible organic solvents or optionally comprising one or more water-miscible organic solvents, if present, in a total amount of up to about 5 % by volume of the total volume, said dispersion having a silica content of at least 20 wt%, said method comprising mixing at least one silane compound and colloidal silica particles in an aqueous silica sol having an S-value from 30 to 90 in a weight ratio of silane to silica from 0.003 to 0.2.
2. A method according to claim 1 , wherein the mixing is carried out at a temperature below about 50° C.
3. A method according to claim 1 , wherein the mixing is carried out at a pH from about 6 to about 12.
4. A method according to claim 1 , wherein said at least one silane compound is an epoxy silane.
5. A method according to claim 1 , wherein said at least one silane compound is an epoxy silane with a glycidoxy group.
6. A method according to claim 1 , comprising mixing an organic binder with the dispersion.
7. A method according to claim 6 , wherein the organic binder is a latex.
8. A stable aqueous silanized colloidal silica dispersion without the presence of any water-miscible organic solvents or optionally comprising one or more water-miscible organic solvents, if present, in a total amount of up to about 5 % by volume of the total volume, said dispersion having a silica content of at least 20 wt% obtained by mixing colloidal silica particles and at least one silane compound in an aqueous silica sol having an S-value from 30 to 90 in a weight ratio of silane to silica from 0.003 to 0.2.
9. A stable aqueous silanized colloidal silica dispersion without the presence of any water-miscible organic solvents or optionally comprising one or more water-miscible organic solvents, if present, in a total amount of up to about 5 % by volume of the total volume, said dispersion having a silica content of at least 20 wt% and having a weight ratio of silane to silica from 0.003 to 0.2, wherein colloidal silica particles are dispersed in a silica sol having an S-value from 30 to 90.
10. A dispersion according to claim 9 , further comprising an organic binder.
11. A dispersion according to claim 9 , further comprising a latex.
12. A dispersion according to claim 9 , wherein the weight ratio of silane to silica is from about 0.006 to about 0.15.
13. A dispersion according to claim 9 , wherein the weight ratio of silane to silica is from about 0.015 to about 0.1.
14. A dispersion according to claim 9 , wherein the silica content in the dispersion is from about 25 to about 70 wt%.
15. A dispersion according to claim 9 , wherein the silica content in the dispersion is from about 30 to about 70 wt%.
16. A dispersion according to claim 1 , wherein the dispersion remains stable for at least 5 months storage at 20° C.
17. A dispersion according to claim 1 , wherein the dispersion viscosity does not increase more than about 40% for a period of at least 4 months storage at 20° C.
18. A dispersion according to claim 9 , wherein the dispersion remains stable for at least 5 months storage at 20° C.
19. A dispersion according to claim 9 , wherein the dispersion viscosity does not increase more than about 40% for a period of at least 4 months storage at 20° C.
20. A dispersion according to claim 17 , wherein the dispersion viscosity does not increase for a period of at least 4 months storage at 20° C.