Porous multilayered hollow fiber and filtration module, and method of manufacturing porous multilayered hollow fiber
View Patent ↗A porous multilayered hollow fiber for outer side pressed filtration is made of a multilayer comprising a supporting layer constituted of the thickness of an expanded porous polytetrafluoroethylene tube, and a filtration layer provided on the outer surface of the supporting layer, wherein pores surrounded by fibrous frameworks in the filtration layer are smaller than those of the supporting layer, and the mean of the maximum fibril length (L) of the fibrous frameworks surrounding each pore in the outer surface of the filtration layer is designed to be small such that (X) and (Y) fall within the range on the XY plane, where (X) is a particle diameter of particles captured when the particle trapping ratio is equal to or more than 90% in the case where the filtration is done under an elevated pressure of 0.1 MPa, and (Y) is a value designated as RFL obtained by dividing (L) by (X). Thus, the degradation of flow rate due to the elapse of time can be prevented, since solid particles to be separated do not enter into pores, and clogging and blockade of the pores do not occur even in the case of filtering a solution of high turbidity. As a result, it is possible to recover filtration property easily by performing back-wash reverse filtration and to maintain excellent filtration property for a long time.
1. A porous multilayered hollow fiber for outer side pressed filtration of solid-liquid separation treatment, the filtration being performed from the outer surface side thereof toward the internal surface side, comprising:
a supporting layer constituted of an expanded porous polytetrafluoroethylene tube (PTFE), and a filtration layer including a porous polytetrafluoroethylene (PTFE) sheet formed by expanding a resin uniaxially or biaxially apart from the supporting layer, the filtration layer being adhered to the outer surface of the supporting layer to form a multilayered body, and pores in the supporting layer three-dimensionally communicating with pores in the filtration layer,
wherein pores surrounded by fibrous frameworks in the filtration layer are smaller than those of the supporting layer, and
the mean maximum length of pores (L) in the outer surface of the filtration layer is designed such that (X) and (Y) fall within the range defined by plotting the following 10 points on the XY plane, where (X) is a particle diameter of particles captured when the particle trapping ratio is equal to or more than 90% in the case where the filtration is done under an elevated pressure of 0.1 MPa, and (Y) is a value designated as RFL obtained by dividing (L) by (X), that is, (Y=L/X): (X, Y)=(0.055, 2) (1, 1.5) (2, 1) (5, 0.5) (10, 0.3) (10, 4) (5, 6) (2, 10) (1, 15) (0.055, 25).
2. A manufacturing method of a porous multilayered hollow fiber, comprising the steps of:
affording an unevenness of 20-200 μm to the outer surface of a porous expanded polytetrafluoroethylene tube by flame treatment, laser irradiation, or plasma irradiation; lapping a porous expanded resin sheet around the outer surface of said porous expanded polytetrafluoroethylene tube;
adhering said porous expanded polytetrafluoroethylene tube and said porous expanded resin sheet together by providing a load thereto after or during such lapping process; and
sintering such adhered tube and resin sheet so as to unite them into a unified body.
3. A porous multilayered follow fiber according to claim 1 , wherein the mean maximum length of pores in said filtration layer is 1% to 30% of the mean maximum length of pores in said supporting layer.
4. A filtration module for outer side pressed filtration or dip-type outer side pressed suction filtration, comprising a bundle consisting of a plurality of porous multilayered hollow fibers according to claim 1 .