Carbon material and method of making same
View Patent ↗The present invention provides a novel carbon material for a electric double-layer capacitor having characteristics entirely different from prior art activated carbon. The capacitor develops a capacitance by a mechanism entirely different from the mechanism of an electric double-layer capacitor using activated carbon. The novel capacitor has improved performance including capacitance. The capacitor has polarized electrodes immersed in an organic electrolyte. The electrodes are made of a nonporous carbon having crystallites of graphite-like carbon. When a voltage is applied, electrolyte ions are intercalated between the layers of the crystallites of the graphite-like carbon together with the solvent. Thus, electric double layers are formed. Intercalation is induced by the first cycle of charging. In the second and following cycles, the capacitance is developed.
1. A method of producing a nonporous carbon having crystallites of a graphite-like carbon and a specific surface area of less than 270 m 2 /g, said crystallites having an interplanar spacing d 002 of 0.360 to 0.380 nm, said method comprising the steps of:
preparing an easily graphitizable carbon in which multilayer crystallites of graphite have been developed;
dry distilling said carbon at 700 C-850 C to obtain a calcined carbon;
treating said obtained calcined carbon with a caustic alkali at 800 C-900 C; and
removing the remaining alkali.
2. A method of producing a nonporous carbon having crystallites of a graphite-like carbon and a specific surface area of less than 270 m 2 /g, said crystallites having an interplanar spacing d 002 of 0.360 to 0.380 nm, said method comprising the steps of:
preparing an easily graphitizable carbon in which multilayer crystallites of graphite have been developed;
dry distilling said carbon at 700 C-850 C to obtain a calcined carbon;
treating said obtained calcined carbon together with a caustic alkali at 800 C-900 C;
removing the remaining alkali to obtain a nonporous carbon; and
treating the obtained nonporous carbon at 500 C-900 C within a reducing atmosphere.
3. A method of producing a nonporous carbon as set forth in claim 1 or 2 , wherein said carbon has a specific surface area of less than 100 m 2 /g.
4. A method of producing a nonporous carbon as set forth in claim 1 or 2 , wherein said caustic alkali is at least one selected from the group consisting of KOH, CsOH, and RbOH.