The invention relates to a chemical vapor deposition process for the continuous growth of a carbon single-wall nanotube where a carbon-containing gas composition is contacted with a porous membrane and decomposed in the presence of a catalyst to grow single-wall carbon nanotube material. A pressure differential exists across the porous membrane such that the pressure on one side of the membrane is less than that on the other side of the membrane. The single-wall carbon nanotube growth may occur predominately on the low-pressure side of the membrane or, in a different embodiment of the invention, may occur predominately in between the catalyst and the membrane. The invention also relates to an apparatus used with the carbon vapor deposition process.
1. A chemical vapor deposition process for the preparation of a single-wall carbon nanotube, comprising:
contacting a carbon-containing gas composition with a porous membrane having a first side and a second side, wherein the first side is opposite to the second side, and wherein a thin catalyst layer is present on at least the first side of the membrane, wherein the thin catalyst layer comprises Al 2 O 3 :Fe in molar ratio from about 50:1 to about 2:1, Al 2 O 3 :Mo in molar ratio from about 100:1 to about 5:1, and Fe:Mo in molar ratio from about 15:1 to about 1:2; and
at a temperature sufficient to decompose said carbon-containing gas composition in the presence of said thin catalyst layer causing growth of a single-wall carbon nanotube,
wherein a pressure differential exists across the porous membrane, the pressure on the second side being less than that on the first side.
2. The process according to claim 1 , wherein said growth of a single-wall carbon nanotube predominantly occurs on the second side of said porous membrane.
3. The process according to claim 1 , wherein said growth of a single-wall carbon nanotube predominantly occurs between the thin catalyst layer and the first side of the porous membrane.
4. The process according to claim 1 , wherein said thin catalyst layer is present only on the first side of said porous membrane.
5. The process according to claim 1 , wherein said carbon-containing gas composition comprises methane gas.
6. The process according to claim 5 , wherein said carbon-containing gas composition comprises methane, hydrogen, and an inert gas.
7. The process according to claim 6 , wherein said inert gas is argon gas.
8. The process according to claim 1 , wherein said porous membrane has a particle size less than about 2 micron.
9. The process according to claim 8 , wherein said porous membrane has a particle size less than about 500 nm.
10. The process according to claim 1 , wherein said porous membrane is selected from the group consisting of: alumina and stainless steel.
11. The process according to claim 1 , wherein said thin catalyst layer is a catalyst composition comprising iron and molybdenum.
12. The process according to claim 11 , wherein said catalyst composition further comprises alumina.
13. The process according to claim 1 , wherein said temperature sufficient to decompose the carbon-containing gas ranges from about 670° C. to about 800° C.
14. The process according to claim 1 , wherein said pressure differential ranges from about 50 to about 500 Torr.
15. The process according to claim 14 , wherein said pressure differential ranges from about 200 to about 300 Torr.
16. The process according to claim 1 , wherein said thin catalyst layer has a ratio of Al 2 O 3 :Fe:Mo of about 9:1:⅓.