View Patent ↗In general terms, the present invention includes a process for producing a new zinc dialkyldithiophosphate (ZDDP) offering improved seal compatibility characteristics in engine and transmission oil packages. The present invention additionally includes zinc dialkyldithiophosphate produced in accordance with the disclosed methodologies, and oil additives, lubricants, and engines and transmission comprising the zinc dialkyldithiophosphate of the present invention.
1. A method for producing a thioacid useful in the production of zinc dialkyldithiophosphate, said method comprising the steps of:
initiating a reaction by introducing a mixture of P 2 O 5 and P 2 S 5 to a solution comprising methyl isobutyl carbinol and isopropyl alcohol;
forming a slurry comprising P 2 O 5 , P 2 S 5 , methyl isobutyl carbinol and isopropyl alcohol;
diluting said slurry by adding an additional quantity of solution comprising methyl isobutyl carbinol and isopropyl alcohol so as to form a dilute slurry; and
forming said thioacid.
2. The method according to claim 1 additionally comprising the step of isolating said thioacid by filtering said dilute slurry.
3. The method according to claim 1 wherein said reaction is conducted in the absence of a catalyst.
4. The method according to claim 1 wherein said mixture of P 2 O 5 and P 2 S 5 comprises, on a weight basis, from about 35 to about 400 parts P 2 S 5 to about 1 part P 2 O 5 .
5. The method according to claim 1 wherein said solution comprising methyl isobutyl carbinol and isopropyl alcohol is an equimolar solution.
6. A method for producing a thioacid useful in the production of zinc dialkyldithiophosphate, said method comprising the steps of:
initiating a reaction by introducing P 2 S 5 into a first solution, wherein said first solution is formed, on a weight basis, by a method comprising the steps of:
creating a mixture comprising from about 35 parts to about 260 parts of methyl isobutyl carbinol to about 1 part P 2 O 5 ; and
forming said first solution by adding 1 part isopropyl alcohol to form about 1.50 to about 1.90 parts of said mixture;
continuing to add P 2 S 5 to said first solution so as to form a slurry;
diluting said slurry by adding additional said first solution so as to form a dilute slurry; and
forming said thioacid.
7. The method according to claim 6 wherein said reaction is conducted in the absence of a catalyst.
8. The method according to claim 6 additionally comprising the step of: isolating said thioacid by filtering said dilute slurry.