Water-soluble film of polyvinyl alcohol
View Patent ↗A water-soluble film made from a resin composition comprising (A) 100 parts by weight of an anionic group-modified polyvinyl alcohol having a viscosity of 10 to 35 mPa·s measured at 20° C. with respect to a 4% by weight aqueous solution thereof, an average degree of hydrolysis of 80.0 to 99.9% by mole and a rate of anionic group modification of 1 to 10% by mole, (B) 20 to 50 parts by weight of a plasticizer, (C) 2 to 30 parts by weight of a filler, and (D) 0.01 to 2.5 parts by weight of a surfactant. The water-soluble film has an excellent water solubility, and is not gelled or insolubilized even if chemicals containing a boric acid substance, particularly sodium perborate, are packaged therein or even if it is put in an aqueous solution of a boric acid substance, particularly sodium perborate.
1. A water-soluble film made from a resin composition comprising (A) 100 parts by weight of a carboxyl group-modified polyvinyl alcohol having a viscosity of 10 to 35 mPa·s measured at 20° C. with respect to a 4% by weight aqueous solution thereof, an average degree of hydrolysis of 80.0 to 99.9% by mole and a rate of anionic group modification of 1 to 10% by mole, (B) 20 to 50 parts by weight of a plasticizer, (C) 2 to 30 parts by weight of a filler, and (D) 0.01 to 2.5 parts by weight of a surfactant, wherein said plasticizer (B) is a mixture of (B1) glycerol with (B2) at least one member selected from the group consisting of trimethylolpropane and diglycerol in a B1/B2 ratio of 25/75 to 75/25 by weight.
2. The film of claim 1 , wherein said rate of anionic group modification is from 2 to 6% by mole.
3. The film of claim 1 , wherein said anionic group-modified polyvinyl alcohol (A) is a carboxyl group-modified polyvinyl alcohol in which the modification is made with a member selected from the group consisting of maleic acid, a maleic acid salt, a monoalkyl maleate and maleic anhydride.
4. The film of claim 1 , wherein said anionic group-modified polyvinyl alcohol (A) is a carboxyl group-modified polyvinyl alcohol in which the modification is made with a monoalkyl maleate.
5. The film of claim 1 , wherein said average degree of hydrolysis is from 90.0 to 98.5% by mole.
6. The film of claim 1 , which is used for packaging a liquid detergent having a pH of 6 to 12 and a water content of less than 10% by weight.