Alkali-free composite sealant materials for solid oxide fuel cells
View Patent ↗A sealant composition for use in sealing solid oxide fuel cells is provided which comprises a glass component which comprises a mixture of alkali-free inorganic oxides, and an optional filler component dispersed in the glass component, said filler component being up to 40% by weight of the composition. The glass component can include, on a mole basis, 20 to 50% BaO, 1 to 10% Y 2 O 3 , 5 to 20% B 2 O 3 , 10 to 30% SiO 2 , 3 to 35% MgO, 2 to 20% CaO, 1 to 10% ZnO, and 0 to 5% ZrO 2 , and exemplary filler components include zirconia, alumina, barium titanate, strontium titanate, and combinations thereof.
1. A glass or glass-ceramic sealant composition comprising:
a glass constituted from a mixture of alkali-free inorganic oxides, the mixture including, on a mole basis, 20 to 50% BaO, 1 to 10% Y 2 O 3 , 5 to 20% B 2 O 3 , 10 to 30% SiO 2 , 3 to 35% MgO, 2 to 20% CaO, 1 to 10% ZnO, and 0 to 5% ZrO 2 , wherein the glass or glass-ceramic sealant composition upon heating to a temperature above its softening point devitrifies and crystallizes, and wherein the glass or glass-ceramic sealant composition is adapted to seal solid oxide fuel cell components.
2. A composite sealant composition comprising:
a glass component constituted from a mixture of alkali-free inorganic oxides, wherein the glass component comprises, on a mole basis, 20 to 50% BaO, 1 to 10% Y 2 O 3 , 5 to 20% B 2 O 3 , 10 to 30% SiO 2 , 3 to 35% MgO, 2 to 20% CaO, 1 to 10% ZnO, and 0 to 5% ZrO 2 ; and
a filler component dispersed in the glass component, said filler component being up to 40% by weight of the composition, wherein the glass component upon heating to a temperature above its softening point will devitrify and crystallize to transform the glass component into a glass-ceramic matrix in which the filler component is dispersed.
3. The composition of claim 1 , wherein the glass component comprises on a mole basis 25 to 35% BaO.
4. The composition of claim 1 , wherein the glass component comprises on a mole basis 1 to 3% Y 2 O 3 .
5. The composition of claim 1 , wherein the glass component comprises on a mole basis 14 to 18% B 2 O 3 .
6. The composition of claim 1 , wherein the glass component comprises on a mole basis 15 to 25% SiO 2 .
7. The composition of claim 1 , wherein the glass component comprises on a mole basis 10 to 20% MgO.
8. The composition of claim 1 , wherein the glass component comprises on a mole basis 10 to 18% CaO.
9. The composition of claim 1 , wherein the glass component comprises on a mole basis 1 to 3% ZnO and 1 to 2% ZrO 2 .
10. The composition of claim 2 , wherein the filler component is non-metal.
11. The composition of claim 2 , wherein the filler component comprises zirconia, alumina, barium titanate, strontium titanate, or a combination thereof.
12. The composition of claim 2 , wherein the filler component comprises yttria-stabilized zirconium oxide.
13. The composition of claim 12 , wherein the filler component further comprises barium titanate.
14. The composition of claim 2 , wherein the glass component and the filler component are mixed with a binder system which comprises one or more thermoplastic polymers.
15. The composition of claim 14 , which is in the form of a tape.
16. A composite sealant composition comprising:
a glass component including, on a mole basis, 25 to 35% BaO, 1 to 3% Y 2 O 3 , 14 to 18% B 2 O 3 , 15 to 25% SiO 2 , 10 to 20% MgO, 10 to 18% CaO, 1 to 3% ZnO, and 1 to 2% ZrO 2 ; and
a filler component dispersed in the glass component, said filler component being up to 40% by weight of the composition.
17. The composition of claim 16 , wherein the filler component is selected from the group consisting of zirconia, alumina, barium titanate, strontium titanate, and combinations thereof.
18. A solid oxide fuel cell stack comprising:
a first structural component;
a second structural component; and
a sealant composition disposed between and contacting the first component and the second component, wherein the sealant composition comprises a glass component which comprises a mixture of alkali-free inorganic oxides, wherein the glass component comprises, on a mole basis, 20 to 50% BaO, 1 to 10% Y 2 O 3 , 5 to 20% B 2 O 3 , 10 to 30% SiO 2 , 3 to 35% MgO, 2 to 20% CaO, 1 to 10% ZnO, and 0 to 5% ZrO 2 ; and a filler component dispersed in the glass component, said filler component being up to 40% by weight of the composition, wherein the glass component upon heating to a temperature above its softening point will devitrify and crystallize to transform the glass component into a glass-ceramic matrix in which the filler component is dispersed.
19. The fuel cell stack of claim 18 , wherein the first component is a first fuel cell and the second component is a separator plate.
20. The fuel cell stack of claim 18 , wherein the first component is a stack of two or more fuel cells and the second component is a manifold for directing fuel and oxidant into and out of the stack.
21. A process for sealing a fuel cell stack, comprising the steps of:
forming a composite sealant mixture comprising a glass component, which comprises a mixture of alkali-free inorganic oxides, wherein the glass component comprises, on a mole basis, 20 to 50% BaO, 1 to 10% Y 2 O 3 , 5 to 20% B 2 O 3 , 10 to 30% SiO 2 , 3 to 35% MgO, 2 to 20% CaO, 1 to 10% ZnO, and 0 to 5% ZrO 2 ; in which a filler component is dispersed, wherein the filler component is up to 40% by weight of the total weight of the glass component and the filler component, wherein the glass component upon heating to a temperature above its softening point will devitrify and crystallize to transform the glass component into a glass-ceramic matrix in which the filler component is dispersed;
applying the composite sealant mixture to a selected location of the fuel cell stack; and
transforming the composite sealant mixture to seal the selected sealant location.
22. The process of claim 21 , wherein the composite sealant mixture is applied in the form of a paste or a tape.
23. The process of claim 21 , wherein the composite sealant mixture further comprises an organic binder material.
24. The process of claim 21 , wherein the transformation step comprises heating the sealant mixture to a temperature above the softening point of the glass component to devitrify and crystallize the glass component, transforming it into a glass-ceramic matrix in which the filler component is dispersed.
25. The process of claim 21 , wherein the seal of the fuel cell stack is effective under pressure differentials up to 5 psig.
26. The composition of claim 2 , wherein a seal formed by the composite sealant composition is effective under a pressure differential up to 5 psig.