Compacted olefin fibers
A polyolefin plaque is made by hot compaction of an assembly of fibres of the oriented polymer. It has been found to be beneficial to subject the fibres to a prior crosslinking process. Hot compaction is then less temperature-sensitive and produces plaques with excellent hot strength properties. Preferably the fibres have been subjected to prior stages of irradiation and annealing, both in a non-oxidising environment, for example acetylene.
1. A polymeric material comprising a compressed assembly of melt formed fibers of a cross-linked oriented polyolefin, the fibers being bound together by a recrystallized melt comprising from 10% to 50% by weight of the polymer in the material, wherein both fibers and recrystallized melt phase are derived by a process comprising:
subjecting molecularly oriented polyolefin fibers to a cross-linking process;
providing an assembly of said cross-linked polyolefin fibers; and
subsequently subjecting said assembly of cross-linked fibers to conditions of temperature and pressure sufficient to melt from 10 to 50% of the polymer in the material and to compact said assembly such that the material is formed.
2. A material as claimed in claim 1 , wherein the crosslinked fibers are radiation crosslinked with ionizing radiation.
3. A material as claimed in claim 1 , wherein the crosslinking step is carried out in an environment which is substantially free of oxygen gas and which comprises a monomeric compound selected from the group consisting of alkynes and alkenes, the alkenes being those having at least two double bonds.
4. A material as claimed in claim 1 , where the fibers have a weight average molecular weight in the range 10,000 to 400,000.
5. A material as claimed in claim 1 , wherein the polyolefin polymer is selected from the group consisting of polypropylene homopolymer, a copolymer containing a major proportion of polypropylene, polyethylene homopolymer and a copolymer containing a major proportion of polyethylene.
6. A material as claimed in claim 1 wherein the polyolefin polymer fibers of the precursor assembly have a gel fraction in the range 0.55 to 0.7.
7. A material as claimed in claim 1 comprising up to 60% by weight of an inorganic filler.