Corrosion-and chip-resistant coatings for high tensile steel
View Patent ↗Corrosion- and chip-resistant coatings for high tensile steel components, such as automotive coil springs, are formed from a coating powder composition of “toughened” epoxy resin. In a single coat embodiment, the entire coating is loaded with at least 75 phr zinc powder. In a dual coat embodiment, an inner coat is loaded with at least 75 phr zinc and an outer, zinc-free coating is reinforced by the addition of fibers and/or by a foaming agent which renders it porous.
1. A chip resistant and corrosion resistant coating on high tensile steel produced from a coating powder composition comprising
(I) 100 weight parts of a resin chosen from:
(i) a resin comprising A) an epoxy resin plus B) a polyhydroxyl functional cross-linker having a hydroxy equivalent weight of from 200 to 500, and
(ii) a resin comprising an adduct of from 75 to 95 wt %, based on the total weight of A) plus B), of an epoxy resin A), and from 5 to 25 wt %, based on the total weight of A) plus B), of an elastomer component B) having a glass-transition temperature of−30° C. or below, and
(II) at least 150 weight parts of zinc powder.
2. The coating according to claim 1 wherein said epoxy resin is a bisphenol A epoxy resin.
3. A method for coating a high-tensile steel surface to provide a chip resistant coating according to claim 2 comprising
applying said coating composition to said surface, and
heating said coating composition to form a coating.
4. The coating according to claim 1 wherein said elastomer component is carboxyl terminated butadiene/acrylonitrile rubber.
5. The coating of claim 1 wherein said composition contains at least 200 weight parts of zinc powder.
6. The coating according to claim 1 wherein said elastomer component has a glass transition temperature of −40° C. or below.
7. A method for coating a high-tensile steel surface to provide a chip resistant coating according to claim 1 comprising
applying said coating composition to said surface, and
heating said coating composition to form a coating.
8. A chip resistant dual coating on high tensile steel comprising a first coat in contact with said high tensile steel and a second outer coat,
said first coat produced from a coating powder composition comprising
(I) 100 weight parts of a resin chosen from:
(i) a resin comprising A) an epoxy resin plus B) a polyhydroxyl functional cross-linker having a hydroxy equivalent weight of from 200 to 500, and
(ii) a resin comprising an adduct of from 75 to 95 wt %, based on the total weight of A) plus B), of an epoxy resin A), and from 5 to 25 wt %, based on total weight of A) plus B), of an elastomer B) component having a glass transition temperature of −30° C. or below, and
(II) at least 75 weight parts of zinc powder, said second coat produced from a coating powder composition comprising
(III) 100 weight parts of a resin chosen from:
(i) a resin comprising A) an epoxy resin plus B) a polyhydroxyt functional cross-linker having a hydroxy equivalent weight of from 200 to 500, and
(ii) a resin comprising an adduct of from 75 to 95 wt %, based on total weight of A) plus B), of an epoxy resin A) plus B), and from 5 to 25 wt %, based on total weight of A) plus B), of an elastomer component having a glass transition temperature of −30° C. or below, said second coating being zinc-free.
9. The coating powder according to claim 8 wherein said epoxy resin of said first coat and of said second coat is a blsphenol A epoxy resin.
10. The coating according to claim 8 wherein said elastomer component of said first coat and of said second coat is carboxyl terminated butadiene/acrylonitrile rubber.
11. The coating of claim 8 wherein the coating composition of said first coat contains at least 150 weight parts of zinc powder.
12. A method for providing a chip resistant coating on high tensile steel according to claim 11 comprising
applying said first coating powder composition to said surface,
applying said second coating powder composition to said first coating composition, and
heating said first and second coating compositions to form a dual coating,
wherein said heating optionally includes heating prior to applying said second coating composition to cure said first coating composition to form said first coat of said dual coating.
13. The coating of claim 8 wherein the coating composition of said first coat contains at least 200 weight parts of zinc powder.
14. The coating according to claim 8 wherein said elastomer component of said first coat and of said second coat has a glass transition temperature of −40° C. or below.
15. The coating according to claim 8 wherein said first coat is between about 1.5 and abaut 3 mils thick and said second coat is from 10 to 15 mils thick.
16. A method for providing a chip resistant coating on high tensile steel according to claim 15 comprising
applying said first coating powder composition to said surface,
applying said second coating powder composition to said first coating composition, and
heating said first and second coating compositions to form a dual coating,
wherein said heating optionally includes heating prior to applying said second coating composition to cure said first coating composition to form said first coat of said dual coating.
17. The coating according to claim 8 wherein said second coat is porous so as to have a density reduced at least 40% relative to theoretical density.
18. The coating according to claim 8 wherein said second coat composition contains from 20 to 80 parts per hundred resin (phr) fibers.
19. A method for providing a chip resistant coating on high tensile steel according to claim 8 comprising
applying said first coating powder composition to said surface,
applying said second coating powder composition to said first coating composition, and
heating said first and second coating compositions to form a dual coating,
wherein said heating optionally includes heating prior to applying said second coating composition to cure said first coating composition to form said first coat of said dual coating.