Zeolite catalyst and preparation process for NO
View Patent ↗A zeolite catalyst and a process for preparing a zeolite catalyst which is both capable of catalyzing the removal of nitrogen oxides from a gaseous medium across a broad temperature range and is operationally and hydrothermally stable at high reaction temperatures. The zeolite catalyst includes a zeolite carrier having a mole ratio of typically from about 14 to about 95 and copper ions supported on the zeolite carrier. The zeolite catalyst is prepared by providing a zeolite carrier, reacting copper with the zeolite carrier by carrying out an ion exchange reaction in a cupric salt aqueous solution at a temperature of between about 4° C. and room temperature (25° C.), and then drying and calcining the catalyst.
1. A process for preparing a catalyst, comprising the steps of:
providing a zeolite carrier having a silicon/aluminum mole ratio of from about 14 to about 95;
providing a cupric salt aqueous solution;
defining a copper zeolite catalyst by carrying out an ion exchange reaction between copper ions and said zeolite carrier in said cupric salt aqueous solution at a temperature of from about 4° C. to about 14° C.; and
calcinating said copper zeolite catalyst.
2. The process of claim 1 wherein said copper zeolite catalyst comprises a copper content of from about 0.1% to about 10.0% by weight.
3. The process of claim 1 wherein said calcining said copper zeolite catalyst comprises calcining said copper zeolite catalyst at a temperature of from about 300° C. to about 700° C.
4. The process of claim 3 wherein said copper zeolite catalyst comprises a copper content of from about 0.1% to about 10.0% by weight.
5. The process of claim 1 wherein said cupric salt aqueous solution is copper sulfate, copper nitrate, copper acetate or copper chloride having a concentration of from about 0.001 molar to about 10 molar.
6. The process of claim 5 wherein said calcining said copper zeolite catalyst comprises calcining said copper zeolite catalyst at a temperature of from about 300° C. to about 700° C.